Tensile properties of several Sn-Ag-Cu lead-free solders have been investigated by micro size specimens. For as-cast specimens, tensile strength increases with increasing content of Cu and Ag. After aging at 120 C for 168 h, however, tensile strengths are similar among eutectic and hypereutectic alloys. The similar tendency was observed among hypoeutectic alloys. Moreover, negligible change was found in tensile strength between specimens aged at 120 C for 168 h and 504 h in all solders. The strength change with aging corresponds to microstructural change of the solder. In the cases of eutectic and hypoeutectic alloys, as-cast microstructures are composed of coarsened primary Sn phases and finer eutectic phases of Sn and intermetallic compounds. The primary Sn phases and the eutectic phases are homogenized upon aging. In contrast, finer Sn and eutectic phases are formed in as-cast hypereutectic alloys. The finer phases are coarsened upon aging. After aging, homogenization of the Sn phases and the eutectic phases occurred in all solders.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.