A diarylethene with a perfluorocyclohexene ring formed hollow crystals by sublimation under normal pressure. Upon UV irradiation of the crystals, they showed remarkable photosalient phenomena and scattered into small pieces. The speed of the flying debris released from the crystal by UV irradiation exceeded several meters per second. To clearly show a photosalient effect resembling the scattering behavior of Impatiens on a smaller scale, small fluorescent beads (1-μm diameter) were inserted into the hollow crystal. Consequently, scattering of the beads was observed as UV irradiation caused deformation and bursting of the hollow structure. This phenomenon is unique to hollow crystals, and the ability to effectively induce remarkable photosalient phenomena is similar to the behavior of hollow-structured Impatiens in nature.
The mechanism of the Brust-Schiffrin gold nanoparticle synthesis has been investigated through the use of ion transfer voltammetry at the water/1,2-dichloroethane (DCE) solution interface, combined with X-ray absorption fine structure (XAFS) of the reaction between [AuCl4](-) and thiol (RSH) in homogeneous toluene (TL) solution. Ion transfer calculations indicate the formation of [AuCl2](-) at RSH/Au ratios from 0.2-2 with a time-dependent variation observed over several days. At RSH/Au ratios above 2 and after time periods greater than 24 h, the formation of Au(I)SR is also observed. The relative concentrations of reaction products observed at the liquid/liquid interface are in excellent agreement with those observed by XAFS for the corresponding reaction in a single homogeneous phase. BH4(-) ion transfer reactions between water and DCE indicate that the reduction of [AuCl4](-) or [AuCl2](-) to Au nanoparticles by BH4(-) proceeds in the bulk organic phase. On the other hand, BH4(-) was unable to reduce the insoluble [Au(I)SR]n species to Au nanoparticles. The number and size of the nanoparticles formed was dependent on the concentration ratio of RSH/Au, as well as the experimental duration because of the competing formation of the [Au(I)SR]n precipitate. Higher concentrations of nanoparticles, with diameters of 1.0-1.5 nm, were formed at RSH/Au ratios from 1 to 2.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.