The effects of test temperature and Sm211 ( 2 BaCuO 5 ) secondary phase particles on the fracture toughness of the Sm123 (SmBa 2 Cu 3 O x ) single grain bulk superconductors were investigated by tensile and bending tests using the V-notched specimens. The correlation between the obtained fracture toughness by tensile and bending test was not necessarily good. The fracture toughness obtained by the indentation method was lower than them. The tensile fracture toughness for the crack propagation in the c-axis, 1.2-1.3 MPa m 1 2 , was higher than that in the direction perpendicular to the c-axis, 1.0-1.1 MPa m 1 2 . Although the former increased with increase in the Sm211 molar fraction, the latter did not increase. There was no appreciable difference between the fracture toughness obtained by the tensile tests at LNT and that at RT, while the fracture toughness from the indentation method at LNT was slightly lower than that at RT.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.