The evolution of ferroelectricity in undoped-HfO2 thin films is systematically studied by controlling the deposition temperature during atomic layer deposition.

The degradation of ferroelectric (FE) properties of atomic layer deposited Hf0.5Zr0.5O2 films with increasing thickness was mitigated by inserting 1 nm-thick Al2O3 interlayer at middle position of the thickness of the FE film. The large Pr of 10 μC/cm2, which is 11 times larger than that of single layer Hf0.5Zr0.5O2 film with equivalent thickness, was achieved from the films as thick as 40 nm. The Al2O3 interlayer could interrupt the continual growth of Hf0.5Zr0.5O2 films, and the resulting decrease of grain size prevented the formation of non-ferroelectric monoclinic phase. The Al2O3 interlayer also largely decreased the leakage current of the Hf0.5Zr0.5O2 films.

Phase change random access memory appears to be the strongest candidate for next-generation high density nonvolatile memory. The fabrication of ultrahigh density phase change memory (≫1 Gb) depends heavily on the thin film growth technique for the phase changing chalcogenide material, most typically containing Ge, Sb and Te (Ge–Sb–Te). Atomic layer deposition (ALD) at low temperatures is the most preferred growth method for depositing such complex materials over surfaces possessing extreme topology. In this study, [(CH3)3Si]2Te and stable alkoxy-Ge (Ge(OCH3)4) and alkoxy-Sb (Sb(OC2H5)3) metal–organic precursors were used to deposit various layers with compositions lying on the GeTe2–Sb2Te3 tie lines at a substrate temperature as low as 70 °C using a thermal ALD process. The adsorption of Ge precursor was proven to be a physisorption type while other precursors showed a chemisorption behavior. However, the adsorption of Ge precursor was still self-regulated, and the facile ALD of the pseudobinary solid solutions with composition (GeTe2)(1‑x)(Sb2Te3) x were achieved. This chemistry-specific ALD process was quite robust against process variations, allowing highly conformal, smooth, and reproducible film growth over a contact hole structure with an extreme geometry. The detailed ALD behavior of binary compounds and incorporation behaviors of the binary compounds in pseudobinary solid solutions were studied in detail. This new composition material showed reliable phase change and accompanying resistance switching behavior, which were slightly better than the standard Ge2Sb2Te5 material in the nanoscale. The local chemical environment was similar to that of conventional Ge2Sb2Te5 materials.

No abstract