In this work, Eu2O3-doped (CaCu3Ti4O12)x of low dielectric loss have been fabricated using both conventional (CS) and microwave sintering (MWS), where x = Eu2O3 = 0.1, 0.2, and 0.3, respectively. According to X-ray diffraction (XRD) and scanning electron microscope (SEM) reports, increasing the concentration of Eu3+ in the CCTO lattice causes the grain size of the MWS samples to increase and vice versa for CS. The X-ray photoelectron spectroscopy (XPS) delineated the binding energies and charge states of the Cu2+/Cu+ and Ti4+/Ti3+ transition ions. Energy dispersive spectroscopy (EDS) analysis revealed no Cu-rich phase along the grain boundaries that directly impacts the dielectric properties. The dielectric characteristics, which include dielectric constant (ε) and the loss (tan δ), were examined using broadband dielectric spectrometer (BDS) from 10 to 107 Hz at ambient temperature. The dielectric constant was >104 and >102 for CS and MWS samples at x > 0.1, respectively, with the low loss being constant even at high frequencies due to the effective suppression of tan δ by Eu3+. This ceramic of low dielectric loss has potential for commercial applications at comparatively high frequencies.
Calcium Copper Titanium Oxide (CaCu3Ti4O12/CCTO) has grasped massive attention for its colossal dielectric constant in high operating frequencies and wide temperature range. However, the synthesis and processing of CCTO directly influence the material’s properties, imparting the overall performance. Researchers have extensively probed into these downsides, but the need for a new and novel approach has been in high demand. Modern synthesis routes and advanced non-conventional sintering techniques have been employed to curb the drawbacks for better properties and performance. This review provides a short overview of the modern synthesis and sintering methods that utilize direct pulse current and electromagnetic waves to improve the material’s electrical, optical, and dielectric properties in the best ways possible. In addition, the current application of CCTO as a photocatalyst under visible light and CuO’s role in the efficient degradation of pollutants in replacement for other metal oxides has been reviewed. This research also provides a brief overview of using CCTO as a photoelectrode in zinc–air batteries (ZAB) to improve the Oxidation-reduction and evolution (ORR/OER) reactions.
The traditional solid-state reaction method was employed to synthesize bulk calcium cobaltite (Ca349/Ca3Co4O9) ceramics via ball milling the precursor mixture. The samples were compacted using conventional sintering (CS) and spark plasma sintering (SPS) at 850, 900, and 950 °C. The X-ray diffraction (XRD) pattern indicates the presence of the Ca349 phase for samples sintered at 850 and 900 °C. In addition, SPS fosters higher densification (81.18%) than conventional sintering (50.76%) at elevated sintering temperatures. The thermo-gravimetric analysis (TGA) and differential thermal analysis (DTA) performed on the precursor mixture reported a weight loss of ~25.23% at a temperature range of 600–820 °C. This current work aims to analyze the electrical properties (Seebeck coefficient (s), electrical resistivity (ρ), and power factor) of sintered samples as a function of temperature (35–500 °C). It demonstrates that the change in sintering temperature (conventional sintering) did not evince any significant change in the Seebeck coefficient (113–142 μV/K). However, it reported a low resistivity of 153–132 μΩ-m and a better power factor (82–146.4 μW/mK2) at 900 °C. On the contrary, the SPS sintered samples recorded a higher Seebeck coefficient of 121–181 μV/K at 900 °C. Correspondingly, the samples sintered at 950 °C delineated a low resistivity of 145–158 μΩ-m and a better power factor (97–152 μW/mK2).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.