The effects of small amounts (up to 5 wt.%) of scandia-and ceria-stabilized zirconia on the electrical conductivity, and the elastic modulus and hardness of yttria-stabilized zirconia were investigated by impedance spectroscopy and nanoindentation tests, respectively. The main purpose of this work was to obtain solid electrolyte compounds with improved properties compared to those of the base materials. Solid electrolytes compounds were prepared by solid-state reaction synthesis with sintering at 1450 ºC for 4 h. All prepared compounds exhibit a cubic fluorite-type structure. The microstructure of the compounds consists of polygonal grains with low (< 2%) porosity. The mean grain size estimated by the intercept method was 5 ± 1 μm. The electrical conductivity of the compound ceramics is lower than that of the base material. Addition of scandia-stabilized zirconia is found to exert a beneficial effect on the matrix by increasing the elastic modulus, achieving 221 MPa for 5 wt.% of the additive.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.