Due to molybdenum’s Body-Centered Cubic (BCC) crystalline structure, its ductile–brittle transition temperature is sensitive to shaping, purity and microstructure. Dense molybdenum parts are usually shaped by the powder metallurgy process. The aim of this work concerns the spark plasma sintering of high-purity powders prepared by inductively coupled plasma. The influence of carbon diffusion and its interaction with oxygen on the density (i.e., the densification stage) and on the microstructure (i.e., the grain growth stage) during spark plasma sintering was investigated. The formation of carbide is usually expected for a sintering temperature above 1500 °C leading to grain growth (e.g., more than 10 times larger than the initial powder grain size after sintering at 1900 °C for 10 min). The brittleness was also affected by the segregation of molybdenum carbides at the grain boundaries (i.e., intergranular brittle fracture). Consequently, to reduce the sintering temperature to below 1500 °C, mechanically activated powders were used. From these milled powders, a dense molybdenum disc (60 mm in diameter and 10 mm in thickness) sintered at 1450 °C under a pressure of 70 MPa for 30 min was obtained. It is composed of a fine microstructure without carbide and oxide, its ductility is close to 13% with a maximum resistance of 550 MPa.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.