We study the effect of carbon to oxygen ratio (C/O) on the electrical resistance of functionalized graphene sheets prepared by thermal exfoliation and reduction of graphite oxide at various temperatures. Using a 2-probe technique in conjunction with Kelvin probe force microscopy, we observe a transition from high-resistance (>400 kΩ/sq) nonlinear current/voltage characteristics at low C/O to low-resistance (<10 kΩ/sq) linear behavior at high C/O, indicating a transition from hopping to diffusive electron transport. Simultaneously, the metal-graphene contacts change from high-resistance Schottky-type behavior to nearly non-invasive metal-metal contact characteristics.
Graphene is a highly attractive candidate for implementation as electrodes in next-generation large-area optoelectronic devices thanks to its high electrical conductivity and high optical transparency. In this study, we show all-solution-processed quantum dot-based lightemitting devices (QD-LEDs) using graphene mono-and multilayers as transparent electrodes. Here, the effect of the number of graphene layers (up to three) on the QD-LEDs performance was studied. While the implementation of a second graphene layer was found to reduce the turn-on voltage from 2.6 to 1.8 V, a third graphene layer was observed to increase the turn-on voltage again, which is attributed to an increased roughness of the graphene layer stack.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.