The nature of Na ion distribution, diffusion path, and the spin structure of P 2-type Na2Ni2TeO6 with a Ni honeycomb network has been explored. The nuclear density distribution of Na ions reveals a 2D chiral pattern within Na layers without breaking the original 3D crystal symmetry, which has been achieved uniquely via an inverse Fourier transform (iFT)-assisted neutron diffraction technique. The Na diffusion pathway described by the calculated iso-surface of Na ion bond valence sum (BVS) map is found consistent to a chiral diffusion mechanism. The Na site occupancy and Ni 2+ spin ordering were examined in detail with the electron density mapping, neutron diffraction, magnetic susceptibility, specific heat, thermal conductivity and transport measurements. Signatures of both strong incommensurate (ICM) and weak commensurate (CM) antiferromagnetic (AFM) spin ordering were identified in the polycrystalline sample studied, and the CM-AFM spin ordering was confirmed by using a single crystal sample through the k-scan in the momentum space corresponding to the AFM peak of ( 1 2 , 0, 1).

We report on the crystal growth and magnetic property studies of layered Na2Ni2TeO6 and Na2Cu2TeO6. The former has a honeycomb layer composed of NiO6 octahedra and the latter is composed of paired CuO4 plaquettes connected through TeO6 octahedra.

No abstract

The control of domain walls is central to nearly all magnetic technologies, particularly for information storage and spintronics. Creative attempts to increase storage density need to overcome volatility due to thermal fluctuations of nanoscopic domains and heating limitations. Topological defects, such as solitons, skyrmions, and merons, may be much less susceptible to fluctuations, owing to topological constraints, while also being controllable with low current densities. Here, we present the first evidence for soliton/soliton and soliton/antisoliton domain walls in the hexagonal chiral magnet Mn 1/3 NbS 2 that respond asymmetrically to magnetic fields and exhibit pair-annihilation. This is important because it suggests the possibility of controlling the occurrence of soliton pairs and the use of small fields or small currents to control nanoscopic magnetic domains. Specifically, our data suggest that either soliton/soliton or soliton/antisoliton pairs can be stabilized by tuning the balance between intrinsic exchange interactions and long-range magnetostatics in restricted geometries.