Carbon molecular sieve and composite carbon molecular sieving membranes are fabricated via the traditional methods of pyrolyzing polymers or by using preceramic composite polymers bearing macromolecular structures. Scant attention is...

This work investigated the long-term hydrothermal performance of composite carbon-SiO2-ZrO2 membranes. A carbon-SiO2-ZrO2 composite was formed from the inert pyrolysis of SiO2-ZrO2-polybenzoxazine resin. The carbon-SiO2-ZrO2 composites prepared at 550 and 750 °C had different surface and microstructural properties. A carbon-SiO2-ZrO2 membrane fabricated at 750 °C exhibited H2 selectivity over CO2, N2, and CH4 of 27, 139, and 1026, respectively, that were higher than those of a membrane fabricated at 550 °C (5, 12, and 11, respectively). In addition to maintaining high H2 permeance and selectivity, the carbon-SiO2-ZrO2 membrane fabricated at 750 °C also showed better stability under hydrothermal conditions at steam partial pressures of 90 (30 mol%) and 150 kPa (50 mol%) compared with the membrane fabricated at 500 °C. This was attributed to the complete pyrolytic and ceramic transformation of the microstructure after pyrolysis at 750 °C. This work thus demonstrates the promise of carbon-SiO2-ZrO2 membranes for H2 separation under severe hydrothermal conditions.

Many researchers regard silica, silica-based and zeolite membranes as the agents that will accomplish H2 separation. These membranes are expected to be productive in various mixture systems and under very...

No abstract

No abstract