Featured Application: Steel slag self-compacting concrete (SSCC) with relatively ideal workability was prepared by substituting steel slag for natural fine aggregate to realize solid waste resource utilization. It is beneficial to solve the problems of steel slag abandonment, land occupation, environment pollution and low utilization rate, and realize utilization of a large amount with low-energy consumption for traditional material saving and sustainable development. SSCC has very high application value and economic significance.Abstract: There is important application value and economic value in exploring the potential use of steel slag to prepare self-compacting concrete (SCC) and make full use of solid waste resources. In this paper, steel slag self-compacting concrete (SSCC) with relatively ideal workability is prepared by using steel slag instead of natural fine aggregate based on mix proportion optimization and SSCC performance research. The filling ability, passing ability and resistance segregation were tested to evaluate the workability of SSCC. The results show that when the content of steel slag sand is 20%, the workability performance of SSCC is similar to that of SCC with natural aggregates. When the content of steel slag sand is less than 60%, the performance of SSCC can also meet the workability requirements after adjusting the amount of raw materials.
This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand (CSLSCC) to prevent the pollution of steel slag in the environment. The SF, J-ring, visual stability index, and sieve analysis tests are primarily employed in this research to investigate the workability of freshly mixed self-compacting concrete containing steel slag at various steel slag sand replacement rates. The experiment results indicate that CSLSCC with the 20% volume percentage of steel slag (VPS) performs better workability, higher strength, and higher specific strength. The 7-day compressive strength of CSLSCC with the 0.4 of the water-binder ratio (W/B), decreases with the increase of steel slag content, while the 28-day compressive strength increases significantly. The ceramsite self-compacting concrete with good comprehensive performance can be obtained when the substitution rate of steel slag sand for fine aggregate is less than 20% (volume percentage).
This study investigated the corrosion behavior of steel rebar in foamed concrete and the effects of water-cement ratio, fly ash, and fiber on reinforced foamed concrete’s corrosion rate and crack width. It was found that the corrosion rate of steel rebar and crack width of foamed concrete increased slowly with time and then developed rapidly, finally growing slowly. The higher the density of foamed concrete, the stronger the corrosion resistance of steel rebar. The best corrosion resistance of steel rebar in foamed concrete is achieved when the water-cement ratio is 0.5, fly ash and fiber are 20% and 0.6%, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.