This study aimed to determine the effect of T6 heat treatment on 7075 aluminum on its hardness and tensile strength. The T6 heat treatment process was heating the test specimens in an oven at various temperatures of the solution heat treatment (SHT) of 350°C, 400°C, 450°C, and 500°C for 2 hours. This process was then followed by quenching for 45 minutes and an artificial aging process at temperature of 120°C for 48 hours. The tests carried out included: Vickers hardness test, tensile test using ASTM B557-84 standard, microstructure test, and XRD test. The test results showed that the hardness and tensile strength before T6 heat treatment were 59.1 VHN and 235.7 MPa, respectively. After the T6 heat treatment was carried out, the hardness results were 105.8, 87.3, 108.9, and 171 VHN and tensile strength of 318.3, 415, 571.7, and 618.3 MPa, respectively. These results indicated that highest hardness was found in the SHT temperature of 500°C, while the increase in tensile strength was found in the temperature of SHT 500°C. It can be obtained because the formation of precipitate after the artificial aging process was due the formation of Al2CuMg and MgZn2.
ABSTRAK Aluminium merupakan logam yang paling banyak digunakan setelah baja, dengan karakteristik utamanya adalah ringan (berat jenis = 2.7 g/cm3), memiliki konduktivitas panas dan listrik yang tinggi, dan ketahanan korosi yang baik. Penggunaan aluminium menempati urutan kedua setelah besi dan baja dan digunakan sebagai bahan untuk komponen industri otomotif, salah satu penggunaanya yaitu berupa komponen pada mobil. Aluminium yang digunakan seri 7075 yang mana memiliki sifat paling baik dan kekuatan paling tinggi dibandingkan paduan aluminium lainnya. Aluminium seri 7075 merupakan seri yang dapat diberikan perlakuan panas, perlakuan panas yang digunakan yaitu tempering dan case hardening, yang mana perlakuan tersebut dapat meningkatkan sifat mekanik aluminium 7075. Metode perlakuan panas yang digunakan yaitu proses tempering case hardening (TCH) dan T6, dengan variasi suhu solution heat treatment (SHT) 3500C, 4000C, 4000C dan 5000C. Proses tempering T6 tahapannya: a). Pemanasan suhu SHT dengan variasi suhu (350 - 5000C), b). Quenching, dan c). Tempering (dengan suhu 1200C selama 2 hari). Sedangkan proses tempering case hardening, proses temper dilakukan setelah proses case hardening dengan metode pack carburizing. Pengujian yang dilakukan yaitu: uji kekerasan vickers, uji tarik, uji struktur mikro dan uji xrd, hasil menunjukkan setelah perlakuan TCH dan T6 didapatkan kekerasan dan kekuatan tarik terbesar pada suhu SHT 500 0C yaitu kekerasannya 182.5 dan 171 VHN, kekuatan tariknya 613.3 dan 618.3 MPa. Kata kunci: Aluminium 7075, Tempering Case Hardening, T6, Kekerasan Vickers, Kekuatan Tarik.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.