Fine energy-level modulations of small-molecule acceptors (SMAs) are realized via subtle chemical modifications on strong electron-withdrawing end-groups. The two new SMAs (IT-M and IT-DM) end-capped by methyl-modified dicycanovinylindan-1-one exhibit upshifted lowest unoccupied molecular orbital (LUMO) levels, and hence higher open-circuit voltages can be observed in the corresponding devices. Finally, a top power conversion efficiency of 12.05% is achieved.

Organic solar cells (OSCs) made of donor/acceptor bulk-heterojunction active layers have been of widespread interest in converting sunlight to electricity. Characterizing of the complex morphology at multiple length scales of polymer:nonfullerene small molecular acceptor (SMA) systems remain largely unexplored. Through detailed characterizations (hard/soft X-ray scattering) of the recordefficiency polymer:SMA system with a close analog, we are able to relate quantitative morphological parameters to the device performance parameters and establish fundamental morphologyperformance relationships that explain why additive use and thermal annealing are needed for optimized performance. A linear correlation between the average purity variations at small length scale (~10 nm) and photovoltaic device characteristics across all processing protocols was observed in ~12%-efficiency polymer:SMA systems. In addition, molecular interactions as reflected by the estimated Flory-Huggins interaction parameters are used to provide context of the room temperature morphology results. Comparison with results from annealed devices suggests that the two SMA systems compared show upper and lower critical solution temperature behavior, respectively. The in-depth understanding of the complex multi-length scale non-fullerene OSC morphology may guide the device optimization and new materials development and indicates that thermodynamic properties of materials systems should be studied in more detail to aid in designing optimized protocols efficiently.

Connections are delineated between solar-cell performance, charge-carrier mobilities, and morphology in a highperformance molecular solar cell. The observations show that maximizing the relative phase purity and structural order while simultaneously limiting the domain size may be essential for achieving optimal solar-cell performances in solution-processed small-molecule solar cells .

Emerging nonfullerene acceptors (NFAs) with crystalline domains enable high-performance bulk heterojunction (BHJ) solar cells. Thermal annealing is known to enhance the BHJ photoactive layer morphology and performance. However, the microscopic mechanism of annealing-induced performance enhancement is poorly understood in emerging NFAs, especially regarding competing factors. Here, optimized thermal annealing of model system PBDB-TF:Y6 (Y6 = 2,2′-((2Z,2′Z)- ((12,13-bis(2ethylhexyl)-3,9-diundecyl-12,13-dihydro-[1,2,5]decreases the open circuit voltage (V OC ) but increases the short circuit current (J SC ) and fill factor (FF) such that the resulting power conversion efficiency (PCE) increases from 14 to 15% in the ambient environment. Here we systematically investigate these thermal annealing effects through in-depth characterizations of carrier mobility, film morphology, charge photogeneration, and recombination using SCLC, GIXRD, AFM, XPS, NEXAFS, R-SoXS, TEM, STEM, fs/ns TA spectroscopy, 2DES, and impedance spectroscopy. Surprisingly, thermal annealing does not alter the film crystallinity, R-SoXS characteristic size scale, relative average phase purity, or TEM-imaged phase separation but rather facilitates Y6 migration to the BHJ film top surface, changes the PBDB-TF/Y6 vertical phase separation and intermixing, and reduces the bottom surface roughness. While these morphology changes increase bimolecular recombination (BR) and lower the free charge (FC) yield, they also increase the average electron and hole mobility by at least 2-fold. Importantly, the increased μ h dominates and underlies the increased FF and PCE. Single-crystal X-ray diffraction reveals that Y6 molecules cofacially pack via their end groups/cores, with the shortest π−π distance as close as 3.34 Å, clarifying out-of-plane π-face-on molecular orientation in the nanocrystalline BHJ domains. DFT analysis of Y6 crystals reveals hole/electron reorganization energies of as low as 160/150 meV, large intermolecular electronic coupling integrals of 12.1−37.9 meV rationalizing the 3D electron transport, and relatively high μ e of 10 −4 cm 2 V −1 s −1 . Taken together, this work clarifies the richness of thermal annealing effects in high-efficiency NFA solar cells and tasks for future materials design.