Fluoride containing resin composites and especially those containing pre reacted glass ionomer fillers could be employed to great benefit in treating high caries risk patients in situations where glass ionomers may be unsuitable; particularly in high load bearing or aesthetically critical locations. SUMMARYAim: To determine the fluoride release and recharge of three fluoride-containing resin composites when aged in deionized water (pH 6.5) and lactic acid (pH 4.0) and to assess mechanical properties of these composites following aging.Methods: Three fluoride-containing resin composites were analyzed in this study; a new giomer material named Beautifil II, Gradia Direct X, and Tetric EvoCeram. A glass ionomer cement, Fuji IX Extra, was also analyzed for comparison. Specimens were fabricated for two test groups: group 1 included 10 disc specimens initially aged 43 days in deionized water (five specimens) and lactic acid (five specimens). The fluoride release from these specimens was measured using a fluoridespecific electrode on nine specific test days during the aging period. Following 49 days of aging, each specimen was recharged in 5000 ppm neutral sodium fluoride solution for 5 minutes. Specimen recharge was then repeated on a weekly basis for 3 weeks. The subsequent fluoride rerelease was measured at 1, 3, and 7 days after each recharge episode. Group 2 included six disc specimens aged for 3 months in deionized water (three specimens) and lactic acid (three specimens). The hardness and elastic modulus of each specimen was measured using nano-indentation at intervals of 24 hours, 1 month, and 3 months after fabrication. Two-way factorial analysis of variance (ANOVA) and post-hoc (Tukey) testing was used to assess the influence of storage media (two levels) and composite type (three levels) on the fluoride release, fluoride rerelease, hardness, and elastic modulus of the assessed materials. The level of significance was set at p¼0.05.Results: All three composites demonstrated fluoride release and recharge when aged in both deionized water and lactic acid. The cumulative fluoride released from Beautifil II into both media was substantially greater than the fluoride released from Gradia Direct X and

No abstract

No abstract

Background: The purpose of this study was to investigate the effect of fluoridated glass fillers on fluoride release, recharge and the flexural properties of modified polymethylmethacrylate (PMMA). Methods: Specimens of PMMA denture base material with various loading of fluoridated glass fillers (0%, 1%, 2.5%, 5% and 10% by weight) were prepared. Flexural properties were evaluated on rectangular specimens (n = 10) aged in deionized water after 24 hours, 1 and 3 months. Disc specimens (n = 10) were aged for 43 days in deionized water and lactic acid (pH 4.0) and fluoride release was measured at numerous intervals. After ageing, specimens were recharged and fluoride re-release was recorded at 1, 3 and 7 days after recharge. Results: Samples containing 2.5%, 5% and 10% glass fillers showed significantly (p < 0.05) greater levels of fluoride release compared with the control and 1% glass fillers specimens. All experimental specimens exhibited fluoride release in both media. The flexural strength of specimens decreased in proportion to the percentage filler inclusion with the modulus of elasticity values remaining within ISO Standard 1567. Conclusions: The modified PMMA with fluoridated glass fillers has the ability to release and re-release fluoride ion. Flexural strength decreased as glass filler uploading increased.Keywords: Flexural strength, fluoride release, glass fillers, modulus of elasticity, polymethylmethacrylate.Abbreviations and acronyms: ANOVA = analysis of variance; PMMA = polymethylmethacrylate; S-PRG = surface pre-reacted giomer.