Heat treatment parameters were varied to determine the effect of normalizing and austenitizing temperature on the properties of an ultra-high strength wrought steel. Normalizing temperature did not have a significant effect on strength and ductility. Higher normalizing temperatures led to an increase in final prior austenite grain size and a slight loss in toughness. Austenitizing temperature of 825 °C was insufficient to produce a fully austenitic structure prior to quenching and led to sub-par impact behavior. The best properties were obtained after austenitizing at 915 °C followed by water quenching; the resulting quasi static properties were shown to be a yield strength of 1380 MPa with an ultimate tensile strength of 1670 MPa and 12.5% total ductility. Charpy V-notch impact properties as high as 52 J at −40 °C and 75 J at 25 °C and the behavior were achieved using higher austenitizing temperatures as well.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.