The influence of curing devices and curing times on the color stability of filling resins was investigated by measuring the CIE-Laboratory-values after performing dry storage, water storage, and a Suntest (EN ISO 7491). Eight samples each of Charisma (CH), Durafill (DU), Definite (DE), and Dyract AP (DY) were light cured by using Translux Energy (TE) for 20, 40 or 60 s, or by using Apollo 95E (AP) for 3, 10 or 20 s. Minor color changes occurred for all dry stored materials, devices and curing times. The TE-cured, water-stored samples behaved similarly to the dry-stored ones, but the samples cured with AP revealed very strong color changes, mainly because of a drastic bleaching process. The bleaching of DU was significantly less than that of the other materials, but a strong white shift occurred. CH, DE, and DU showed very little (and even acceptable) discolorations after the Suntest when TE-cured. DY showed a drastically discoloration. All samples cured using AP drastically bleached and shifted to white for DU and DY but to dark for DE. In conclusion, the extent of discoloration depends on (i) the material, (ii) the test method, (iii) curing time, and (iv) the curing device. The halogen light-cured samples performed best.
PurposeTo investigate the antibacterial effect and the effect on the material properties of a novel delivery system with Irgasan as active agent and methacrylated polymerizable Irgasan when added to experimental dental resin composites.Materials and MethodsA delivery system based on novel polymeric hollow beads, loaded with Irgasan and methacrylated polymerizable Irgasan as active agents were used to manufacture three commonly formulated experimental resin composites. The non-modified resin was used as standard (ST). Material A contained the delivery system providing 4 % (m/m) Irgasan, material B contained 4 % (m/m) methacrylated Irgasan and material C 8 % (m/m) methacrylated Irgasan. Flexural strength (FS), flexural modulus (FM), water sorption (WS), solubility (SL), surface roughness Ra, polymerization shrinkage, contact angle Θ, total surface free energy γS and its apolar γS
LW, polar γS
AB, Lewis acid γS
+and base γS
- term as well as bacterial viability were determined. Significance was p < 0.05.ResultsThe materials A to C were not unacceptably influenced by the modifications and achieved the minimum values for FS, WS and SL as requested by EN ISO 4049 and did not differ from ST what was also found for Ra. Only A had lower FM than ST. Θ of A and C was higher and γS
AB of A and B was lower than of ST. Materials A to C had higher γS
+ than ST. The antibacterial effect of materials A to C was significantly increased when compared with ST meaning that significantly less vital cells were found.ConclusionDental resin composites with small quantities of a novel antibacterially doped delivery system or with an antibacterial monomer provided acceptable physical properties and good antibacterial effectiveness. The sorption material being part of the delivery system can be used as a vehicle for any other active agent.
All materials met the corresponding requirement in ISO 4049. Filler load negatively correlated with water sorption but not with solubility. There was an influence of the resin matrix, too. No significant differences were found between composites, ormocers, and compomers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.