Poly(lactic) acid (PLA) film with 2 wt% mixed carbon nanofillers of graphene nanoplates (GNPs) and multiwall carbon nanotubes (MWCNTs) in a weight ratio of 1:1 with impurities of fullerene and carbon black (CB) was produced by layer-to-layer deposition and hot pressing. The release of carbon nanoparticles from the film was studied at varying time-temperature conditions and simulants. Migrants in simulant solvents were examined with laser diffraction analysis and transmission electron microscopy (TEM). Film integrity and the presence of migrants on the film surfaces were visualised by scanning electron microscopy (SEM). The partial dissolution of PLA polymer in the solvents was confirmed by swelling tests and differential scanning calorimetry (DSC). Nanoparticle migrants were not detected in the simulants (at the LOD 0.020 μm of the laser diffraction analysis) after migration testing at 40°C for 10 days. However, high-temperature migration testing at 90°C for 4 h provoked a release of GNPs from the film into ethanol, acetic acid and oil-based food simulants. Short carbon nanotubes were observed rarely to release in the most aggressive acetic acid solvent. Obviously, the enhanced molecular mobility at temperatures above the glass transition and partial dissolution of PLA polymer by the food simulant facilitate the diffusion processes. Moreover, shape, size and concentration of nanoparticles play a significant role. Flexible naked GNPs (lateral size 100-1000 nm) easily migrate when the polymer molecules exhibit enhanced mobility, while fibrous MWCNTs (> 1 μm length) formed entangled networks on the film surfaces as the PLA polymer is partly dissolved, preventing their release into food simulants. The impurities of fullerenes and CB (5-30 nm) were of minor concentration in the polymer, therefore their migration is low or undetectable. The total amount of released migrants is below overall migration limits.
The study compared the effects of swelling and dissolution of a matrix polymer by food simulants on the release of graphene nanoplates (GNPs) and multiwall carbon nanotubes (MWCNTs) from poly(lactic) acid (PLA) and polypropylene (PP) composite films. The total migration was determined gravimetrically in the ethanol and acetic acid food simulants at different time and temperature conditions, while migrants were detected by laser diffraction analysis and transmission electron microscopy. Swelling, thermal analysis, and scanning electron microscopy were applied to characterize the degradation of polymer films at the migration conditions. The release of nanoparticles was found in a high‐temperature migration test of 4 h at 90 °C. The hydrolytic dissolution of the PLA polymer in the food simulants caused a migration of GNPs (>100 nm) from the PLA/GNP/MWCNT films into the simulant solvents, while the entangled MWCNTs formed a network on the film surface, preventing their migration from the PLA composite films. In contrast, the PP polymer slightly swells in ethanol solvents, allowing some short carbon nanotubes to be released from the surface and cut edges of the PP/MWCNT film into food simulants. Mathematical modeling of diffusion was applied that accounts for type of polymer, time–temperature conditions, and solvent concentration; model parameters were validated with experimental results. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 45469.
Nanoparticles of graphene and carbon nanotubes are attractive materials for the improvement of mechanical and barrier properties and for the functionality of biodegradable polymers for packaging applications. However, the increase of the manufacture and consumption increases the probability of exposure of humans and the environment to such nanomaterials; this brings up questions about the risks of nanomaterials, since they can be toxic. For a risk assessment, it is crucial to know whether airborne nanoparticles of graphene and carbon nanotubes can be released from nanocomposites into the environment at their end-life, or whether they remain embedded in the matrix. In this work, the release of graphene and carbon nanotubes from the poly(lactic) acid nanocomposite films were studied for the scenarios of: (i) biodegradation of the matrix polymer at the disposal of wastes; and (ii) combustion and fire of nanocomposite wastes. Thermogravimetric analysis in air atmosphere, transmission electron microscopy (TEM), atomic force microscopy (AFM) and scanning electron microscope (SEM) were used to verify the release of nanoparticles from nanocomposite films. The three factors model was applied for the quantitative and qualitative risk assessment of the release of graphene and carbon nanotubes from nanocomposite wastes for these scenarios. Safety concern is discussed in respect to the existing regulations for nanowaste stream.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.