Flexural strength and fracture toughness of molybdenum disilicide and its composites with 10 wt% TiB 2 and 10 wt% TiB 2 ؉ 10 wt% SiC, synthesized by the hot-pressing technique, were evaluated as a function of temperature, ranging from ambient temperature to 1600°C. Results show that the composites have higher strength and slightly lower toughness as compared with monolithic MoSi 2 at room temperature. At high temperatures, the composites exhibit higher strength as well as higher toughness vis-à-vis monolithic MoSi 2 . Among the composites, the double reinforcement of SiC and TiB 2 was found to be more effective in improving the mechanical properties. A transition from brittle to ductile behavior was observed at temperatures greater than 1300°C for all materials tested. The high-temperature mechanical behavior was found to be significantly influenced by the flow of an intergranular glassy phase and the attendant cavity nucleation and growth along the grain boundaries. Micromechanisms responsible for the ambient as well as the elevated-temperature property improvement in composites are discussed with the aid of fractography.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.