An anion exchange membrane was prepared by the chloromethylation and the amination of polyvinyl chloride (PVC), as the base polymer. The membrane properties of the prepared anion exchange membrane, including ionic conductivity, ion exchange capacity, and water content were measured. The ionic conductivity of the prepared anion exchange membrane was in the range of 0.098×10 −2 -7.0×10 −2 S cm −1 . The ranges of ion exchange capacity and water content were 1.9-3.7 meq./g-dry-membrane and 35.1-63.1%, respectively. The chemical stability of the prepared anion exchange membrane was tested by soaking in 30 wt% KOH solution to determine its availability as a separator in the alkaline water electrolysis. The ionic conductivity during the chemical stability test largely did not change.
Abstract:We investigated the variation of anion exchange membrane of hydrogen generator of alkaline electrolysis. We detected the variation of elements and change of anion exchange membrane using EDS and FE-SEM. We detected two different sites of membrane because of different structure of membrane. Sp1 shows that the distribution ratio of C, O, Al is 98% very higher than Sp2 of 78%. Especially, the main elements of STS316 which is P, S, Fe, Ni were more detected at Sp2 than Sp1. We think that this result depends on the structure of membrane. This also affect the resistance, lifetime of membrane and decrease the efficiency of hydrogen production. We hope that this article is a foundation of developing of hydrogen production technology.
>> This study was performed to observe the change of stainless steel pipe interacting with alkaline solution. We used STS316L and STS304 as samples which were soaked in alkaline solution. We measured the samples by use of FE-SEM, EDX, SIMS to observe the surface and depth profile of both samples. The result showed that the precipitate appeared on the surface of both samples from 5 days. but the precipitate was confirmed to be decreased as time passes. but the quantitative change of precipitates at both samples was different as time passed. The EDX showed that the precipitate is Potassium from solution of Electrolysis. The result also showed that the primary elements of stainless steel pipeline and of Alkaline Solution were changed. The change of primary elements was severe between 5 days to 16 days and was stable around 40 days at both samples. The reaction of STS316L with alkaline solution was lower than STS304. We hoped that this study would be the foundation of developing the electrode of the alkaline hydrogen generator.
In this paper, We studied the change of surface and variation of elements on both electrodes of hydrogen generator of alkaline electrolysis in use of FE-SEM and SIMS. We used the stainless steel 316(600 μ m) as electrode in condition of 25%KOH, 60℃ Temperature. The results show that the intensity of elements (C, Si, P, S, Ti, Cr, Mn, Fe, Ni, Mo) of Positive Electrode are decreased as much as about 10 1 ∼10 3 than the original electrode. Thickness of Positive Electrode is decreased about 40 μm after chemical reaction. The negative electrode, however, shows a slight variation in the intensity of elements (C, Si, P, Fe, Ni, Mn, Mo) but Change of thickness and surface' shape of electrode show nothing after chemical reaction. The change in thickness and variation of Stainless Steel 316 cause the lifetime of electrode to be shorted. We also observed hydrogen, oxygen, potassium in both electrodes. Especially, The potassium is increased in proportional with depth of positive electrode. this means the concentration of alkali solutions is changed. and so we have to supply alkaline solution to generator in order to produce same quantity of hydrogen gas continuously. we hope that this study gives a foundation to develop the electrode for hydrogen generator of alkaline electrolysis.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.