Thin-walled copper tubes are usually produced by multi-pass float-plug drawing deformation. In general, the annealing treatment subsequently is necessary to release the stored energy and adjusts the microstructure. In this study, an investigation on the evolution of annealing twins as well as textures in the thin-walled (Ф6 mm × 0.3 mm) copper tube underwent holding time-free heat treatment was reported. Electron backscattered diffraction analysis reveals that a large number of Σ3 boundaries (60° 〈111〉 twin relationship) are produced at the early stage of heat treatment, which is due to the lower boundary energy. With the recrystallization proceeding, the migration rate of grain boundaries decreases on account of the grain growth; meanwhile, the unique Σ9 boundaries (38.9° 〈110〉 relationship) are formed due to the interaction of the Σ3 boundaries. As a result, the number fractions of Σ3 boundaries and high-angle grain boundaries decrease rapidly. During the grain growth stage, a strong recrystallization texture was formed due to the fact that the grains of Goss orientation have a growth advantage over the others. As a result, the initial copper texture was transferred into the Goss texture in domination.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.