PURPOSEThis in vitro study aimed to compare the failure load and failure characteristics of two different zirconia framework designs of premolar crowns when subjected to static loading.MATERIALS AND METHODSTwo types of zirconia frameworks, conventional 0.5 mm even thickness framework design (EV) and 0.8 mm cutback of full contour crown anatomy design (CB), were made for 10 samples each. The veneer porcelain was added on under polycarbonate shell crown made by vacuum of full contour crown to obtain the same total thickness of the experiment crowns. The crowns were cemented onto the Cobalt-Chromium die. The dies were tilted 45 degrees from the vertical plane to obtain the shear force to the cusp when loading. All crowns were loaded at the lingual incline of the buccal cusp until fracture using a universal testing machine with cross-head speed 0.5 mm/min. The load to fracture values (N) was recorded and statistically analyzed by independent sample t-test.RESULTSThe mean and standard deviations of the failure load were 1,170.1 ± 90.9 N for EV design and 1,450.4 ± 175.7 N for CB design. A significant difference in the compressive failure load was found (P<.05). For the failure characteristic, the EV design was found only cohesive failures within veneering porcelain, while the CB design found more failures through the zirconia framework (8 from 10 samples).CONCLUSIONThere was a significant difference in the failure load between two designs, and the design of the framework influences failure characteristic of zirconia crown.
This study aimed to examine the shear bond strength between cobalt chromium alloy and autopolymerizing acrylic resin using experimental primers containing 5, 10, and 15 wt% of 4-methacryloxyethyl trimellitic anhydride or 1, 2, and 3 wt% of 3-methacryloxypropyl-trimethoxysilane comparison to 5 commercial primers (ML primers, Alloy primer, Metal/Zirconia primer, Monobond S, and Monobond plus). Sixty alloy specimens were sandblasted and treated with each primer before bonded with an acrylic resin. The control group was not primed. The shear bond strengths were tested and statistically compared. Specimens treated with commercial primers significantly increased the shear bond strength of acrylic resin to cobalt chromium alloy (p<0.05). The highest shear bond strength was found in the Alloy primer group. Among experimental group, using 10 wt% of 4-methacryloxyethyl trimellitic anhydride -or 2 wt% of 3-methacryloxypropyltrimethoxysilane enhanced highest shear bond strength. The experimental and commercial primers in this study all improved bonding of acrylic resin to cobalt chromium alloy.
This study evaluated the oxide characteristics on a Ag-Sn particle surface modified by acid and heat in order to understand the bonding mechanism. Nine different Ag-Sn particles including standard Sn, SnO and SnO2 were evaluated by X-ray Photoelectron Spectroscopy (XPS). The particles were also used for preparing the composite to test the flexural properties following the ISO4049.A high correlation between flexural strength of the composites and Sn3d binding energy of their filler particles was found.Different oxide forms (SnO and SnO2) showed different adhesive abilities to bond with 4-META, regarding the difference in flexural strength of the composite.The highest flexural strength composite showed Sn3d binding energy of its filler at 486.4eV, which was the SnO binding area. This implies that SnO was responsible for a good bond between particle surface and 4-META coupling agent.
PURPOSEThis study evaluated the depth of cure of resin composite cured by light through a translucent fiber post.MATERIALS AND METHODSThe opaque plastic tubes in various lengths of 2, 4, 6, 8, 10, 12, 14 mm. were filled with resin composite in which two different translucent fiber posts were inserted into the center and photo-polymerized for 40 seconds. The degree of conversion of the cured composite at bottom surface were examined using Fourier transform infrared attenuated total reflection spectrometer (FTIR/ATR) at 0.1, 0.5 and 1.0 mm apart from the post surface.RESULTSThe degree of conversion of the 0.1 mm, 0.5 mm, 1.0 mm apart from the post surface was highest at the 2 mm level and continuously decreased when the distance from the light source was increased and drastically decreased when the depth from the top of the post was greater than 4-6 mm. For each level, the highest degree of conversion was at 0.1 mm from the post surface and decreased continuously when the distance apart from the post surface was increased.CONCLUSIONThe quantity of light transmission depends on the type of post and the light transmission capability of the post, especially after 4-6 mm depth and the area further apart from the post surface, are insufficient for clinical light activation of resin composite.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.