Poly(hydroxyalkanoates) PHAs are synthesized by many bacteria as inclusion bodies and their biodegradability and structural diversity have been studied with a view to their potential application as biodegradable materials. A method based on FT-IR was developed to carry out rapid qualitative and quantitative analysis of PHAs in Pseudomonas, when they were grown on sodium octanoate. Using absorbance of the ester band of PHAs, a rapid method was reported to distinguish PHB and PHO and to determine polymer content in intact bacteria. Relative areas in which the C=O area was normalized to the area of the peak representing the amid group (1656 cm(-1)) characteristic of bacteria were calibrated to the polymer content which was determined after solvent extraction. Polymer contents vary from 0% to 53% and depend on the nature of the bacteria. Among 27 strains of Pseudomonas belonging to the rRNA homology group I, a very low amount of bacteria were able to produce PHB. The majority of strains were able to produce a copolymer, PHO, in which the major constituent unit is 3-hydroxyoctanoate. The FT-IR results were further confirmed by gas chromatography analysis after methanolysis of polymer, but FT-IR method requires less preparation of sample than gas chromatography and it is very useful for screening a large variety of Pseudomonas.

No abstract

Summary: Novel polyester and copolyesters have been prepared by anionic ring‐opening polymerization of racemic 4‐alkyloxycarbonyl‐3,3‐dimethyl‐2‐oxetanones that had been synthesized in five steps from diethyl oxalpropionate used as chemical precursor. The anionic polymerizations, realized in bulk or in solution with tetraethylammonium benzoate as initiator, led to a homopolymer and copolymers with high molecular weights and polydispersity indices close to unity. These features can be explained by the presence of two methyl groups on the same carbon atom in the lactone, preventing transfer reactions to the monomer. Preparation of seeds and re‐initiation by addition of fresh monomer confirmed a living process. The hydrolysis of poly[(R,S)‐3,3‐dimethylmalic acid] under physiological conditions yielded (R,S)‐3,3‐dimethylmalic acid. A terpolymer was also prepared for biological studies related to its use as biodegradable materials for tissue regeneration.Structure of poly[(R,S)‐3,3‐dimethylmalic acid].imageStructure of poly[(R,S)‐3,3‐dimethylmalic acid].

No abstract

The segmental motions of flexible chains in the lamellar structure of a strongly segregated poly(styrene)-poly(dimethylsiloxane) (PS-PDMS) diblock were investigated over a time scale of a few tens of microseconds. (2)H NMR experiments were performed on the PDMS block, selectively perdeuterated. Transverse relaxation measurements show that the main part of the PDMS repeat units display anisotropic reorientational motions within the diblock lamellae and such a segmental ordering essentially results from interchain steric repulsions. (2)H double quantum-based experiments evidenced a non-uniform local stretching of PDMS chains and enabled the underlying distribution of the orientational order parameter to be determined quantitatively. Besides, a fraction of the PDMS chain segments, about 14%, were found to display isotropic - or nearly isotropic - reorientations, which could be assigned to repeat units located within a thin sublayer (about 1-2 nm) at the lamellae midplane, but also deeper in the lamellae, close to folded parts of the chains. These experimental results were confronted to theoretical descriptions of opposing polymer brushes and, in particular, to the strong-stretching theory (SST) including the entropic contribution of free chain ends.

No abstract

No abstract

No abstract