The Petroleum Development Oman (PDO) operates assets worth US$18 billion in South of Oman. The majority of the producing wells, nearly 60% of them, are highly oil producer when fitted with ESP completion. The intending desired operating life of these wells is greater than 25-years. Field histories showed that 5 casings failure per year in Field X were mainly directly attributed due to onset of severe electrochemical corrosion. A field campaign of downhole logs recorded throughout the field indicated a potentially more severe risk of failures prevailed for outermost barriers within its initial 3 to 5 years of the production life. This sleeping threat was mainly due to setup of long line corrosion cells activity on well casings due to their direct contact with aquifers. The associated corrosion rate found to be abnormally high. The concentric casings set across these aquifers showed generalized wall thinning; which was not confined to any single aquifer; rather entire well structure failure saw across several consecutive aquifers. This observation was in contrary to mostly prevailing phenomena of Middle Eastern historical fields where usually a single aquifer acts as anode. A few wells in Field X failed at much deeper, across unexpected formation zones, creating a mystery about the corrosion mechanism. High rate of casing failures in closely spaced wells left no room for infill drilling. Since the asset was contributing a prime role in Oman's economy such high number of well failures was serious concern for the operator. Therefore, there was a strong need to put an end to casing failures after reaching out to the root cause of mechanism triggering these failures.In an attempt to solve the problem acquired well integrity logs were uploaded into a dynamic multiwell data base to study; wall loss correlation with formations, affect of completion on downhole corrosion. Moreover, it was intended to find any well to well correlation if any; and to study aerial and lateral trend of corrosion and rate. The outcome of this exercise indicated strong correlation between external corrosion and wells fitted with downhole ESP motors and where water cut was high. Various ultrasonic imaging logs acquired for production casing indicated a direct relation seen between power cable insulation degradation; resulting in leakage/stray currents to flow on casing; and severe damage to well structures. To explore further in that direction downhole investigation trials were conducted with potential profile logs on several wells to depicate the axial current profile changes when electrical submersible pump motors of nearby offset wells were turned ON and OFF. Trials confirmed ESP role and a very striking SPE-172736-MS
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.