The effects of heat treatment process on the microstructure and mechanical properties of S47450 bolt materials were studied by optical microscope (OM), scanning electron microscope (SEM), X-ray diffraction (XRD), tensile test, impact test and hardness test. The results showed that in the temperature range selected by the test, the quenched martensite of the bolt material after quenching at 1070 °C and tempering at 670 °C was fully refined and evenly distributed, and the precipitation of Cr23C6 played the role of precipitation hardening. It showed the excellent comprehensive mechanical properties, with the Brinell hardness reaching 295 HBW and the tensile strength of 1035 MPa. The elongation was 16 %, and the impact energy at room temperature was 21 J.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.