Abstract. The corrosion behavior of mild steel in seawater was investigated using an immersion test and energy-dispersive X-ray spectroscopy in solutions from the sites of Muara Baru, Suramadu and Tol Mandara. As reference, solutions of 3.5% and 5% NaCl were prepared. Dissolved oxygen, salinity, conductivity, and total dissolved solids (TDS) were measured. It was found that uniform corrosion occurred on the mild steel during the immersion test. The corrosion resistance of the steel decreased with increasing exposure time. Since the magnitudes of conductivity, salinity and TDS of all test solutions were similar, it was concluded that dissolved oxygen (DO) and chloride ions play an essential role in inducing the corrosion risk of mild steel. Both parameters hinder the formation of a stable passive film on the surface of corroded mild steel.
Abstract. This paper reports the influence of Mo and Ni on the tensile properties of the modified 13Cr martensitic stainless steels in tempered condition. Four steels with different content of Mo and Ni were prepared by induction melting followed by hot forging, quenching and tempering. The experimental results showed that the addition of about 1% and 3% Mo has a beneficial effect to increase both the tensile strength and the elongation of the steels. On the contrary, the addition of about 3% Ni into the martensitic stainless steel results in decreasing of both the tensile strength and the elongation. Among the alloys investigated the 13Cr3Mo type steel exhibited largest tensile strength of 1348 MPa and largest elongation of 12%. The observation on the tensile fractured surfaces by using scanning electron microscope supported these findings.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.