Calcium phosphate (CaP)-based bioceramics are the most widely used synthetic biomaterials for reconstructing damaged bone. Accompanied by bone healing process, implanted materials are gradually degraded while bone ultimately returns to its original geometry and function. In this progress report, we reviewed the complex and tight relationship between the bone healing response and CaP-based biomaterials, with the emphasis on the in vivo degradation mechanisms of such material and their osteoinductive properties mediated by immune responses, osteoclastogenesis and osteoblasts. A deep understanding of the interaction between biological healing process and biomaterials will optimize the design of CaP-based biomaterials, and further translate into effective strategies for biomaterials customization.
The study assessed the bonding performance of three universal adhesives on desensitized dentin with etch-and-rinse mode or self-etch mode after nano-hydroxyapatite (nHAp)-based desensitizers application. Simulated sensitive dentin specimens were prepared and separated into four groups: no treatment as the negative control, groups desensitized by Biorepair toothpaste, Dontodent toothpaste, or nHAp paste. Three universal adhesives of All-Bond Universal, Single Bond Universal, and Clearfil Universal Bond with etch-and-rinse or self-etch mode were bonded to the desensitized dentin specimens separately, followed by resin composite build-ups. Micro-tensile bond strength was measured using a micro-tensile tester. The wettability of desensitized dentin was evaluated by the contact angle of the adhesives. Resin infiltration was observed by confocal laser scanning microscopy. Dentin tubular occlusion and nanoleakage were observed by scanning electron microscope. The results showed that the etch-and-rinse or self-etch mode of each adhesive showed similar bond strength when bonding to nHAp-based desensitized dentin. The dentin surface was partially covered by desensitizers after desensitization. Compared with the self-etch mode, stronger demineralization and more reopened dentin tubules were observed in the etch-and-rinse mode after acid etching; longer resin tags and more nanoleakage in the resin–dentin interface were observed when using the etch-and-rinse mode. When bonding to nHAp-based desensitized dentin with universal adhesives, no significant difference in bond strength was found between self-etch mode or etch-and-rinse mode; while the latter produced more nanoleakage in the resin–dentin interfaces.
The study evaluated the effect of calcium-based desensitizing toothpastes on the dentinal tubule occlusion and its influence on the dentin bond strength of universal adhesive. Mid-coronal dentin samples were prepared for hypersensitivity model and treated by the following calcium-based desensitizing toothpastes: no treatment (Control), Clinpro (fTCP), Pro-Relief (Pro-Argin), and Repair & Protect (Novamin).Single Bond Universal adhesive was applied in self-etch or etch-and-rinse mode.The dentinal tubule occlusion and adhesion interface were evaluated under scanning electron microscope (SEM). A double-fluorescence technique was used to examine interfacial permeability under confocal laser scanning microscopy (CLSM).The micro-tensile bond strength (μTBS) was employed, followed by the fracture interface observation. SEM showed the toothpastes occluded dentinal tubules, and the occlusion exhibited stability against acid and abrasion. Hindered resin infiltration was observed in the adhesion interface after desensitization. CLSM showed more water permeation within or under the adhesion interface in etch-and-rinse mode than self-etch mode. Desensitization decreased the μTBS in self-etch mode.When using etch-and-rinse mode, the desensitized samples presented similar μTBS to the control group. No difference in μTBS was found between the two bonding modes, except for the control group. Calcium-based desensitizing toothpastes can effectively occlude the exposed dentinal tubules with acid-resistant and abrasionresistant stability. The desensitization reduced the dentin bond strength of the universal adhesive system in self-etch mode but did not affect the bond strength of etch-and-rinse mode.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.