As the key half reaction of water-splitting electrolysis, the hydrogen evolution reaction (HER) that occurs at the cathode directly determines the overall efficiency of hydrogen production. To improve the efficiency...
Ti-6Al-4V is widely used in various fields of modern industry, but it is difficult to obtain an ultra-smooth surface of Ti-6Al-4V due to its poor machinability. In this article, ultraviolet-induced (UV-induced) nanoparticle colloid jet machining was utilized to carry out ultra-precision polishing of Ti-6Al-4V to improve the surface quality. The results of infrared differential spectroscopy before and after polishing show that new chemical bonds such as Ti-O-Ti (Al-O-Ti and V-O-Ti) appear on the Ti-6Al-4V workpiece surface, which indicates that the material of Ti-6Al-4V workpiece is removed through the chemical interaction between TiO2 nanoparticles and workpiece surface in the process of UV-induced nanoparticle colloid jet machining. The comparison of metallographic structure of Ti-6Al-4V before and after polishing shows that the chemical activity and material removal rate of the primary α phase in Ti-6Al-4V is higher than that of the remnant β phase in UV-induced nanoparticle colloid jet machining, which lead to the well-distributed nano-scale surface peaks and valleys at regular intervals on the polished Ti-6Al-4V workpiece surface. After polishing, the longitudinal residual stress on the surface of Ti-6Al-4V workpiece decreases from 75 MPa to 67 MPa and the transverse stress decreases from 13 MPa to 3 MPa. The surface roughness of Ti-6Al-4V workpiece is reduced from Sa 76.7 nm to Sa 2.87 nm by UV-induced nanoparticle colloid jet machining.
In this paper, ultraviolet (UV)-induced nanoparticle colloid jet machining is proposed to achieve ultrasmooth surface polishing by using the interaction between nanoparticles and the workpiece surface under the action of the ultraviolet field and the hydrodynamic pressure field. In the process of UV-induced nanoparticle colloid jet machining, the effects of photocatalysis on the interaction between nanoparticles and the workpiece surface need to be further studied in order to better understand the polishing process. This paper presents the interaction between TiO2 nanoparticles and a Si workpiece surface with and without ultraviolet irradiation. Scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS) were applied to investigate the differences in the interaction of TiO2 nanoparticles with Si workpieces. The SEM and XPS results indicate that the photocatalysis of UV light can promote the interaction between TiO2 nanoparticles and a Si surface by creating more interfacial reaction active centers between the TiO2 nanoparticles and the Si workpiece. The FT-IR and XPS spectra show that TiO2 nanoparticles are chemically bonded to the Si workpiece by oxygen-bridging atoms in Ti-O-Si bonds. Due to the effects of photocatalysis, UV-induced nanoparticle colloid jet machining has a higher polishing efficiency than nanoparticle colloid jet machining with the same polishing parameters.
Electric field enhanced ultraviolet (UV)-induced nanoparticle colloid jet machining is proposed to improve the material removal efficiency of UV-induced nanoparticle colloid jet machining by applying an external electric field. The influences of TiO2 nanoparticle concentration, applied electric field voltage and pH value for the photocatalytic activity of the polishing slurry was investigated by orthogonal experiments. Terephthalic acid (TPA) was used as a fluorescent molecular probe to reflect the relative concentration of hydroxyl radical groups (ꞏOH) in polishing slurry, which directly affects the material removal rate in the UV- induced nanoparticle colloid jet machining process. Scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS) were employed to inspect the interaction variations between the TiO2 nanoparticles and the SiC workpiece surface. The SEM and XPS results exhibit that the external electric field can enhance the adsorption of TiO2 nanoparticles on the SiC workpiece surface, which can create more interfacial reaction active centers in the polishing process. The FT-IR spectra results indicate that TiO2 nanoparticles were chemically bonded to the SiC surface by oxygen-bridging atoms in Ti-O-Si bonds. The results of fixed-point polishing experiment show that due to the enhancement effect of external electric field on the photocatalytic activity of the polishing slurry, the material removal efficiency of electric field enhanced UV- induced nanoparticle colloid jet machining is 15% higher than that of UV- induced nanoparticle colloid jet machining, and is 28% higher than that of pure nanoparticle colloid jet machining. Atomic force microscope (AFM) micromorphology show that an ultra-smooth SiC workpieces with surface roughness of Rms 0.84nm (Ra 0.474nm) has been obtained by electric field enhanced UV-induced nanoparticle colloid jet machining.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.