The sintering of ultrafine γ‐Al2O3 powder (particle size ∼10–20 nm) prepared by an inert gas condensation technique was investigated in air at a constant heating rate of 10°C/min. Qualitatively, the kinetics followed those of transition aluminas prepared by other methods. Measurable shrinkage commenced at ∼ 1000°C and showed a region of rapid sintering between ∼1125° and 1175°C followed by a transition to a much reduced sintering rate at higher temperatures. Starting from an initial density of ∼0.60 relative to the theoretical value, the powder compact reached a relative density of 0.82 after sintering to 1350°C. Compared to compacts prepared from the as‐received powder, dispersion of the powder in water prior to compaction produced a drastic change in the microstructural evolution and a significant reduction in the densification rate during sintering. The incorporation of a step involving the rapid heating of the loose powder to ∼1300°C prior to compaction (which resulted in the transformation to α‐Al2O3) provided a method for significantly increasing the density during sintering.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.