In this study, a reformer stack was made by incorporating silicon technology into catalyst preparation. The volumes of an individual micro-channel chip and a whole reformer stack were 0.4 cm3 and 16 cm3, respectively. Different weight ratios (B/C = 35, 15, 5, and 0 wt%) of binder (a mixture of boehmite, bentonite, and deionized water) and catalyst were mixed to find out the optimal adhesion between the catalyst and silicon substrate. The results from this study show that the percentage of weight loss of the catalyst on the silicon substrate increases as the concentration of inorganic binder decreases. To further increase the exposed surface area of the catalyst deposited on the micro-channels, micro-column structures were integrated into the channels; however, a blockage of the catalysts among the columns during deposition was encountered. To resolve this issue, a method of pre-protecting the micro-channel with thick-film photoresist was utilized for the catalyst deposition, and the performance of the fabricated micro-column reformer was able to reach a 95% methanol conversion rate, 90% hydrogen selectivity, and 1.6 × 10−5 (mol min−1) hydrogen yield at 225 °C in the partial oxidation of methanol reaction.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.