Equiatomic CuZr alloy undergoes a martensitic transformation from the B2 parent phase to martensitic phases (P21/m and Cm) below 150 °C. We clarified the effect of the thermal cycling on the morphology and crystallography of martensite in equiatomic CuZr alloy using a transmission electron microscopy. The 10th cycled specimens consisted of different multiple structures at the maximum temperature of differential scanning calorimetry (DSC) measurement −400 °C and 500 °C, respectively. At the maximum temperature 400 °C of DSC measurement, it is composed of the fine plate-like variants, and a lamellar eutectoid structure consisting of Cu10Zr7 and CuZr2 phases on the martensitic variant. Concerning the maximum temperature of 500 °C of DSC measurement, it is observed the martensitic structure and the lamellar structure in which the martensitic phase was completely eutectoid transformed. The formation of this lamellar eutectoid structure, due to thermal cycling leads to the shift of forward and reverse transformation peaks to low and high temperature side. In addition, new forward and reverse transformation peaks indicating a new transformation appeared by thermal cycling, and the peaks remained around −20 °C. This new martensitic transformation behavior is also discussed.
We investigated the texture and the shape change in the equiatomic TiPd alloy, and discussed the relationship between the shape change and the atomic movements associated with martensitic transformation. Thermomechanical analyzer tests indicate that the direction of the shape change was different between the 0° and 90° samples, cutting out parallel and perpendicular to the hearth side of button ingot, respectively. In the 0° sample, shrinking and expansion were observed during the reverse and forward martensitic transformations, respectively, whereas the opposite tendency was confirmed in the 90° sample compared to the 0° sample. During the isobaric test, the martensitic variants were oriented to a (010) plane with compressive loading, and the B2 parent phase crystals also became coarse. There is a close relationship between the shape change due to the crystal orientation by the isobaric test and the shear-shuffling direction due to martensitic transformation.
Equiatomic CuZr alloy undergoes a martensitic transformation from the B2 parent phase to martensitic phases (P21/m and Cm) below 150 °C. We clarified the effect of the thermal cycling on the morphology and crystallography of martensite in equiatomic CuZr alloy using a transmission electron microscopy. The 10th cycled specimens consisted of different multiple structures at the maximum temperature of DSC measurement: 400 °C and 500°C, respectively. At the maximum temperature 400 °C of DSC measurement, it is composed of the fine plate-like variants, and a lamellar eutectoid structure consisting of Cu10Zr7 and CuZr2 phases on the martensitic variant. Concerning the maximum temperature 500 °C of DSC measurement, it is observed the martensitic structure and the lamellar structure in which the martensitic phase was completely eutectoid transformed. The formation of this lamellar eutectoid structure due to thermal cycling leads to the shift of forward and reverse transformation peaks to low and high temperature side. In addition, new forward and reverse transformation peaks indicating a new transformation appeared by thermal cycling, and the peaks remained around -20 °C. This new martensitic transformation behavior is also discussed.
Keywords: CTEM (conventional transmission electron microscopes), crystal structure, LPSO (long period stacking ordered structure) TEM specimen preparation; the disk with a diameter of 3 mm was dimpled with a GATAN Model 656 and Ar ion milled with a GATAN model 695 PIPSII TEM utilized; JEM 2000FX, JEM 2100PLUS (200 kV, JEOL Ltd.)
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.