As unpredictable fracture of the front axle will lead to serious safety accidents, its failure behavior study is essential. This paper analyzes typical cracks on I-shaped and leaf springs of the front axle made by Steel A and Steel B. Steel B has a lower content of S, N, Cu, and Sn than Steel A. In order to identify the failure mechanism difference, the low magnification etch test, and metallographic and scanning electron microscope analyses were conducted. The results show that the microstructures are tempered sorbite, and the cracks are with intergranular fracture characteristics. The aggregated distribution of sulfide inclusions in the matrix of Steel A is higher than that of Steel B. Copper-rich particles are detected in the cracks of Steel A. The result indicates that the purity distinction of raw steel can have a big difference on the cracking rate of the front axle even under the same manufacturing process. Relevant suggestions to reduce the cracking are put forward from the aspects of raw materials and process conditions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.