Ultra-thin epitaxial NiSi2 was formed, and its structure was examined by electron microscopy and x-ray diffraction. Compared with previous reports, the measured resistivity of the epitaxial NiSi2 was unprecedentedly low, reaching 7 μΩ cm in the experimental results and up to 14.93 μΩ cm after modification. The reliability, which was investigated under different temperatures and current densities to understand its electronic characteristics, was 1.5 times better than that of the conventional polycrystalline counterpart. Black's equation and the measured mean-time-to-failure (MTTF) were used to obtain the reliability characteristics of epitaxial and poly-NiSi2. Confidence intervals at 95% for each MTTF confirmed the single failure mode. The electromigration phenomenon was observed to be the failure mechanism. Our results provide evidence that epitaxial NiSi2 is a promising contact material for future electronics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.