We report on the fabrication and characterization of AlGaN/GaN metal-insulator-semiconductor (MIS) capacitors and high-electron-mobility transistors (MIS-HEMTs) using a 5 nm thick Al2O3 dielectric deposited by cost-effective and environmental-friendly mist chemical vapor deposition (mist-CVD) technique. Practically hysteresis-free capacitance–voltage profiles were obtained from the fabricated two-terminal MIS-capacitors indicating high quality of the mist-Al2O3/AlGaN interface. Compared with reference Schottky-gate HEMTs, mist MIS-HEMTs exhibited much improved performance including higher drain current on-to-off ratio, much lower gate leakage current in both forward and reverse directions and lower subthreshold swing. These results demonstrate the potential and viability of non-vacuum mist-CVD Al2O3 in the development of high-performance GaN-based MIS-HEMTs.

We report on the impact of the 3-nm-thick ex-situ AlGaN regrown layer prior to insulator deposition on the interfacial properties of Al2O3/AlGaN/GaN metal-insulator-semiconductor (MIS) structures. MIS-capacitors (MIScaps) with regrown AlGaN layer exhibited anomalously excessive threshold voltage shift compared to reference sample without regrown AlGaN, suggesting highly reduced interface states density (Dit). Moreover, MIScaps with regrown AlGaN layer exhibited “spill-over” in the capacitance-voltage (C-V) profiles, further evidencing the improved Al2O3/AlGaN interfaces. Fabricated three-terminal MIS-HEMTs with regrown AlGaN showed less hysteresis in transfer curves, enhanced maximum drain current, and increased linearity over the reference device.

No abstract

No abstract