Photocatalytic reaction at 298 K by platinum-loaded titanium(IV) oxide (TiO 2 -Pt) particles suspended in deaerated aqueous solutions of 2-propanol or (S)-lysine (Lys) was investigated. The TiO 2 catalysts with various amounts of Pt loadings were prepared by impregnation from aqueous chloroplatinic acid solution onto a commercial TiO 2 (Degussa P-25) followed by hydrogen reduction at 753 K. The physical properties of deposited Pt, e.g., particle size, surface area, and electronic state, were studied respectively by transmission electron microscopy, volumetric gas adsorption measurement, and X-ray photoelectron spectroscopy as well as infrared spectroscopy of adsorbed carbon monoxide. The increase in Pt amount mainly resulted in an increase of the number of Pt deposits, not of their size. The catalysts were suspended in the aqueous solutions and photoirradiated at a wavelength >300 nm under an argon (Ar) atmosphere. The overall rate of photocatalytic reactions for both 2-propanol and Lys, corresponding to the rate of consumption of these substrates, was negligible without Pt loading, increased drastically with the loading up to ca. 0.3%, and was almost constant or a little decreased by the further loadings. However, the rate of formation of pipecolinic acid (PCA) from Lys was improved gradually with a increase of Pt loading up to ca. 2 wt %. These dependences were discussed as a function of Pt surface area, which is employed as a measure that includes the properties of both number and size of Pt deposits. For the photocatalytic dehydrogenation of 2-propanol, the rate dependence could be interpreted semiquantitatively with the model that only the TiO 2 particles loaded with at least one Pt deposit can photocatalyze, but the reaction rate is independent of the number of Pt deposits. Therefore, the overall rate is proportional to the number of Pt-loaded TiO 2 particles. On the other hand, for the interpretation of the rate of PCA and H 2 productions, the number of Pt deposits on each TiO 2 particle had to be taken into account. The efficient production of PCA at higher Pt loadings was attributed to the reduction of a Schiff base intermediate produced via oxidation of Lys with positive holes and subsequent intramolecular condensation at the Pt deposit that is close to the site for the oxidation. Otherwise, photoexcited electrons are consumed for H 2 production and the intermediate remains unreduced or undergoes further oxidation. It was suggested that the intermediate produced at the TiO 2 surface sites within a distance of several nanometers from the Pt deposit undergoes efficient reduction to PCA. Thus, the importance of the distribution of Pt deposits for the preparation of highly active and selective TiO 2 -Pt photocatalyst has been clearly demonstrated.