This paper proposes a novel methodology to synthesize highly fluorescent gold nanoparticles (NPs) with a maximum quantum yield of 16%, in the near-infrared (IR) region. This work discusses the results of using our (previously developed) matrix sputtering method to introduce mercaptan molecules, α-thioglycerol, inside the vacuum sputtering chamber, during the synthesis of metal NPs. The evaporation of α-thioglycerol inside the chamber enables to coordinate to the "nucleation stage" very small gold nanoclusters in the gas phase, thus retaining their photophysical characteristics. As observed through transmission electron microscopy, the size of the Au NPs obtained with the addition of α-thioglycerol varied from approximately 2-3 nm to approximately 5 nm. Plasmon absorption varied with the size of the resultant nanoparticles. Thus, plasmon absorption was observed at 2.4 eV in the larger NPs. However, it was not observed, and instead a new peak was found at approximately 3.4 eV, in the smaller NPs that resulted from the introduction of α-thioglycerol. The Au NPs stabilized by the α-thioglycerol fluoresced at approximately 1.8 eV, and the maximum wavelength shifted toward the red, in accordance with the size of the NPs. A maximum fluorescent quantum yield of 16% was realized under the optimum conditions, and this value is extremely high compared to values previously reported on gold NPs and clusters (generally ∼1%). To our knowledge, however, Au NPs of size>2 nm usually do not show strong fluorescence. By comparison with results reported in previous literature, it was concluded that these highly fluorescent Au NPs consist of gold-mercaptan complexes. The novel method presented in this paper therefore opens a new door for the effective control of size, photophysical characteristics, and structure of metal NPs. It is hoped that this research contributes significantly to the science in this field.
Production of oxygen-deficient tungsten
oxide nanoparticles with
a diameter of around 10 nm have been successfully developed using
a microwave-induced plasma in liquid technique. The prepared blue-green
nanoparticles exhibit strong absorption in the visible region; thus,
these could be efficient visible-light photocatalysts. The high-angle
annular dark-field images revealed the dislocation of tungsten, which
causes oxygen deficiencies.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.