Demand for rapid and massive-scale exfoliation of bulky graphite remains high in graphene commercialization and property manipulation. We report a procedure utilizing “preformed acidic oxidizing medium (PAOM)” as a modified version of the Hummers’ method for fast and reliable synthesis of graphene oxide. Pre-mixing of KMnO4 and concentrated H2SO4 prior to the addition of graphite flakes enables the formation of effectively and efficiently oxidized graphene oxide (EEGO) featured by its high yields and suspension homogeneity. PAOM expedites diffusion of the Mn-oxidants into the graphite galleries, resulting in the rapid graphite oxidation, capable of oxidizing bulky graphite flakes (~0.8 mm in diameter) that can not be realized by the Hummers’ method. In the scale-up tests, ten-time amount of graphite can be completely exfoliated by PAOM without need of extended reaction time. The remarkable suspension homogeneity of EEGO can be exploited to deposit ultra-flat coating for wafer-scale nanopatterning. We successfully fabricated GO optical gratings with well-defined periodicity (300 nm) and uniform thickness (variation <7 nm). The combination of the facile and potent PAOM approach with the wafer-scale patterning technique may realize the goal for massive throughput graphene nanoelectronics.
An Au/K bicatalyst-assisted chemical vapor deposition process using C 2 H 2(g) to grow high-density carbon nanocoils (CNCs) uniformly on the fibers in carbon fiber cloth substrates three-dimensionally was developed. An as-deposited substrate (2.5 × 1.0 cm 2 ) showed a high electrochemical active surface area (16.53 cm 2 ), suggesting its potential usefulness as the electrode in electrochemical devices. The unique one-dimensional (1D) helical structure of the CNCs shortened the diffusion pathways of the ions in the electrolyte and generated efficient electron conduction routes so that the observed serial resistance R s was low (3.7 Ω). By employing two-electrode systems, a liquid-state supercapacitor (SC) in H 2 SO 4(aq) (1.0 M) and a solid-state SC with a polypropylene (PP) separator immersed in H 2 SO 4(aq) (1.0 M)/polyvinylalcohol were assembled and investigated by using CNC-based electrodes. Both devices exhibited approximate rectangular shape profiles in the cyclic voltammetry measurements at various scan rates. The observations indicated their electric double-layer capacitive behaviors. From their galvanostatic charge/discharge curves, the specific capacitances of the liquid SC and the solid SC were measured to be approximately 137 and 163 F/g, respectively. In addition, the solid-state CNC-based SC possessed excellent energy density (15.3 W h/kg) and power density (510 W/kg). The light weight solid SC (0.1965 g, 2.5 × 1.0 cm 2 ) was bendable up to 150° with most of the properties retained.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.