Repeated mechanical scission and recombination of dynamic covalent bonds incorporated in segmented polyurethane elastomers are demonstrated by utilizing a diarylbibenzofuranone-based mechanophore and by the design of the segmented polymer structures. The repeated mechanochemical reactions can accompany clear colouration and simultaneous fading.

The orientation and crystallization of regioregular poly(3-dodecylthiophene) (P3DDT) in different diameter nanopores were investigated. P3DDT nanowires were prepared by a melt-wetting nonporous alumina template with P3DDT melts. The microstructure of the nanowires was analyzed by micro-Fourier transform infrared spectroscopy, grazing incidence wide angle X-ray diffraction, and differential scanning calorimetry. Although Form I modification prevails in all the nanowires, Form I crystals decrease and Form II crystals increase as the pore diameter decreases. The crystallites developed in the nanowires preferentially aligned with π-π stacking (b-axis) along the long axis of the wire and this orientation is marked as the wire diameter decreases. These results could provide guidance on designing polymeric nanomaterials for functional nanodevices in high performance organic photovoltaic cells, sensors, and electrodes.

The effect of molecular weight on the molecular aggregation structure of polymers bearing a pendant perylenediimide (PDI) side chain, designated PAc12PDI, was investigated using synchrotron radiation X‐ray diffraction measurements. It was found that depending on molecular weight, either the main chain axis or the side chain axis behaves as the longitudinal axis in fiber samples and was aligned parallel to the fiber axis. A similar phenomenon is present in thin film samples, but was complicated by the additional influence of the interfacial free energy of the side chain group. Even in the case of the polymer with lower molecular weight, the face plane of PDI was found to show both parallel and perpendicular orientations to the substrate (i.e., flat‐on and edge‐on orientations). On the other hand, if the length of the main chain is sufficiently long with respect to the length of the side chain, the face plane of PDI was oriented perpendicular to the substrate, leading to an edge‐on orientation in the thin film. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016, 54, 2275–2283

No abstract

No abstract

No abstract

No abstract

No abstract