A new core-shell nanostructure consisting of inorganic hydroxyapatite (HAP) nanoparticles as the core and organic alginate as the shell (denoted as HAP@Alg) was successfully synthesized by a pre-gel method and applied to pH-responsive drug delivery systems (DDS). HAP@Alg nanoparticles have the advantages of hydroxyapatite and alginate, where hydroxyapatite provides pH-responsive degradability, and alginate provides excellent biocompatibility and COOH functionality. Through the subsequent addition of CaCl(2) and phosphate solutions to the alginate solution, HAP@Alg nanoparticles with controllable particle sizes (ranging from 160 to 650 nm) were obtained, and their core-shell structure was confirmed through transmission electron microscopy (TEM) observation. Rhodamine 6G (R6G), a positively charged dye, was selected as a model drug for pH-sensitive DDS. R6G was encapsulated in the HAP/Alg nanoparticles upon synthesis, and its loading efficiency could reach up to approximately 63.0%. The in vitro release behavior of the loaded R6G at different pH values was systematically studied, and the results indicated that more R6G molecules were released at lower pH conditions. For example, after releasing for 8 h, the release amount of R6G at pH 2.0 was 2.53-fold the amount at pH 7.4. We attributed this pH-sensitive release behavior to the dissolution of the HAP core in acidic conditions. The results of the MTT assay and confocal laser scanning microscopy indicated that the HAP@Alg were successfully uptaken by liver cancer cells (HepG2) without apparent cytotoxicity. The synthesized HAP@Alg nanoparticles show great potential as drug nanovehicles with high biocompatibility, enhanced drug loading, and pH-responsive features for future intracellular DDS.
We report synthesis of hollow calcium phosphate (CaP) nanospheres with high surface area by using block copolymer micelles as templates. The obtained CaP nanospheres exhibit very high biocompatibility, showing great promise for intracellular bio-applications in future.
Polymeric micelles consisting of asymmetric triblock copolymers were successfully used for fabrication of robust hybrid nanoparticles with highly biocompatible calcium phosphate shells. The hydrophobic polystyrene core encapsulates hydrophobic fluorescent dyes such as Nile red. The anionic polyacrylic acid provides the site for the mineralization reaction of calcium phosphate. The polyethylene glycol corona stabilizes the hybrid nanoparticles. Fluorescent dyes can be used as imaging agents for determining the location of the nanoparticles and to give an observable indication of drug delivery, while the calcium phosphate shell can enhance the fluorescence of the encapsulated dye.
Polymeric micelles with core–shell–corona nanoarchitecture were designed for intracellular therapeutic anti-cancer drug carriers. Poly(styrene-b-acrylic acid-b-ethylene glycol) (PS-b-PAA-b-PEG) asymmetric triblock copolymer underwent self-assembly in aqueous solution to form spherical micelles with hydrophobic PS core, anionic PAA shell and hydrophilic PEG corona. The anti-cancer drug (doxorubicin, DOX) was successfully incorporated into the polymeric micelles. The in vitro release experiment confirmed that the release of DOX from the micelles was inhibited at pH 7.4. In contrast, an accelerated release of DOX was observed at mildly acidic conditions such as pH 4.5. The excellent biocompatibility of our PS-b-PAA-b-PEG-based micelles made the synthesized nano-carrier best suited for the delivery of anti-cancer drugs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.