The microgroove cannot be observed on the polyimide film surface. Therefore the cause of liquid crystal orientation is due to the polymer molecule of polyimide film via Ink-jet Printing Method arranged in order primarily. The different performances of polyimide film between the rubbing and ion-beam processed were also investigated. Meanwhile, the related real panels will exhibit in SID 2005, too. 1.Introduction Alignment process is a necessary procedure in the manufacture LCD industry. There are two purposes with alignment process. One is joined the orientational order of LC to the molecular order at the PI film surface when the applied voltage was less that the threshold voltage. The other one is asked the LC molecules to recovery the initial state distinctly when the applied voltage was released. Hence the performance of LCD was determined by the alignment ability of LC molecules. Nevertheless, the size of glass substrate is larger and larger, and the traditional rubbing process will show difficulties like roller bending. Ion-beam-processed was used to substitute for rubbing process.Ink-jet printing technology is also able to correspond with the greater size panel. Comparing commercial APR printing process with ink-jet technology, as shown in Figures 1(a) and 1(b), respectively. The maximum utility rate of polyimide for ink-jet process is up to 95%, which is higher than that for the commercial process ca 25%. Even though ink-jet process has great competitive advantage, however the uniformity of coating film associated with the stage-moving rate, droplet frequency and material properties is still unstable so that the use of polyimide film coating with ink-jet technology is a growing challenge in modern digital display. With coating polyimide film via ink-jet process, whereas the phenomena of coffee-ring and non-uniformity in film thickness would be the problems. To resolve these problems, the approach of pattern design and adjusting process parameters is significant.The subject of this study is to investigate the probability of next generation with ion-beam-processed and polyimide film ink-jet printing technology. (a) (b) Figure 1 The (a) APR printing and (b) ink-jet Process of polyimide film coating. Experimental ProceduresThe indium-tin-oxide (ITO)-coated glass substrates with a substrate dimension of 74 54 3 mm 3 were employed to manufacture the test panels. The substrates were spin-coated with JSR polyimide, then were baked, cured and carried out the ion-beam-processed. The ion-beam species used for this research was argon. The 90° TN test panels were consisted of two substrates with directs of ion-beam irradiation perpendicular each other, and the cell gap was maintained at ca 4 µm by using ball spacers. In addition, the 90° TN test panels were filled with nematic Merck's LC.There are incident ion-beam angle, vacuum pressure, stage-moving rate, etc. regarding the ion-beam-processed, and one of the certain notable factor is incident ion-beam angle. In this investigation, the parameters of incident ion-beam a...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.