In this study, the effects of micro‐Al2O3 (MA) and nano‐Al2O3 (NA) on the mechanical properties and durability performance of a mortar containing fly ash (FA) were investigated. In the first step, MA and NA were added to the mortar (as a cement replacement) at dosages of 0%, 5%, 10% and 15% by weight. The flowability of the mixture containing NA and MA showed a dosage‐dependent behavior, and the addition of MA resulted in a higher flow spread compared with NA. The flow spread increased at 5% (for both NA and MA), and a further increase in the particle content to 10% and 15% decreased the flow spread value. Although the presence of MA and NA contributed to increasing the compressive strength as the particle content increased, the addition of NA resulted in a greater increase in compressive strength (40% increase when adding 15% of NA). The highest splitting tensile strength was obtained when 10% NA was used, and a further increase in the particle content decreased the splitting tensile strength. In the optimization step, the effect of a binder replacement with FA (10, 20 and 30%) in the presence of 10% NA as the optimum level of additive was investigated. Generally, the addition of FA decreased the compressive strength. The highest drop in compressive strength was noticed at early ages, and there was no significant difference in strength development from 14 days to 28 days. A decreasing trend in the splitting tensile strength was observed with the addition of FA content.
<p><b>Direct reduction (DR) of iron ore with hydrogen is a promising alternative ironmaking process with near-zero CO2 emissions. This approach is applicable for the reduction of New Zealand (NZ) titanomagnetite (TTM) ironsand, which offers the potential for establishing a clean steelmaking industry in NZ. However, iron ore fines must first be agglomerated into pellets to provide a porous medium for reducing gases in a DR shaft reactor. Pelletization is currently the most widely used process for agglomeration of fine concentrates. In this process, iron ore particles are balled into green pellets that are strengthened through induration at high temperature. The main challenges with pelletization are the selection of a binder that provides the required pellet strength without causing contamination, and the large energy consumption associated with induration. The optimum pelletizing conditions also differ between iron ore types as they have distinct physical and chemical characteristics. </b></p> <p>This work investigates into the pelletization and sintering behaviour of NZ TTM ironsand. Ironsand pellets were initially bonded with sodium bentonite clay and carboxymethyl-cellulose (Peridur) to analyse the effects of various ironsand particle size, sintering temperature, and sintering duration. It was found that ironsand with an average particle size of 65 µm was optimal in producing green pellets with high strength. The compressive strength of these pellets after sintering at 1200 °C in air for 2 hr was measured to be 976 N, which is well above the strength requirement for pellet feedstock in a shaft reactor. This strength was attributed to the recrystallisation of titanohematite grains from oxidation of TTM, and formation of a liquid bonding phase by the melted binders in the interparticle regions. </p> <p>Building on the results, alternative binders and additives were then explored to potentially lower the sintering temperature requirement. A combination of both organic binder and inorganic additive was found essential in meeting the target strength at each stage of pelletization. Organic binders such as carboxymethyl-cellulose enhanced the strength of green pellets by increasing the liquid viscosity between the particles which led to greater interparticle forces. Inorganic additives, such as bentonite, calcium borate and ground glass, promoted high sintered strengths by melting and forming additional bonding bridges. Microwave heating was then investigated as a potential low-energy alternative to a conventional induration process. NZ TTM ironsand pellets were sintered in a prototype microwave furnace. It was found that the sintered strength could be increased by incorporating alumina balls with the pellet feed. The microwave transparent alumina balls allowed the uniform distribution of heat amongst the pellets and reduced the thermal load along the length of the cavity. Plasma production occurred due to the high power concentrated in the cavity which also increased the strength of sintered pellets. The high temperature from the plasma allowed the binder to melt into a liquid bonding phase. However, excessive exposure to plasma caused the ironsand particles to form a highly dense structure that affected the reducibility of pellets in hydrogen. </p> <p>In summary, the findings in this thesis provide a general understanding of the pelletizing and subsequent sintering behaviour of NZ TTM ironsand. The production of ironsand pellets that meet the target strength is entirely feasible. This knowledge can be applied in the future where a feedstock of NZ ironsand pellets is required in an industrial hydrogen-based DR process. The induration of pellets in a prototype microwave furnace was also demonstrated, and the results show promise for further development of microwave heating as an alternative approach to pellet induration.</p>
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.