In this paper, an inexpensive, simple and well-accurate process of the generation of bimetallic silver Ag//gold Au core//shell is colloidal metal nanoparticles (MNPs). This is achieved via an atmospheric pressure non-thermal plasma glow discharge between two electrodes. One of these electrodes is a capillary tube placing over solution about (1 cm) that acts as the cathode, while the other electrode is a metal disk immersed in the solution and acts as an anode. Glow discharge process carried out at room temperature using a home-made cell with (6 KV) applied voltage and direct current (DC) about (1.8 mA) for different discharge periods. A wide range of bimetallic Ag//Au colloidal MNPs was rapidly synthesized as a result of non-thermal plasma formation between a capillary tube and the surface of AgNO3 solution for (5 min) and a mixture of AgNPs-HAuCl4 solution for (5, 10 and 15 min). Field emission scanning electron microscope (FE-SEM), transmission electron microscope (TEM) and X-ray diffraction were used to investigate the structural properties of the bimetallic Ag//Au colloidal MNPs. While optical properties were investigated using a UV-Vis spectrophotometer. Results show that the discharge time plays a crucial role in modifying the bimetallic nanoparticles properties such as grain size, surface area, and optical stability. Moreover, TEM and FE-SEM confirm the formation of Ag//Au core//shell structure with uniform sizes and shapes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.