a b s t r a c tAntimicrobial packaging materials were obtained by incorporation of lysozyme into cellulose acetate (CA) films. In order to achieve controlled release of lysozyme, the structure of the films was changed from highly asymmetric and porous to dense by modulating the composition of the initial casting solution. The highest release rate, soluble lysozyme activity and antimicrobial activity were obtained with the film prepared from 5% CA solution including 1.5% lysozyme. Increasing CA content in the casting solution decreased the porosity of the films, hence, reduced the release rate, maximum released lysozyme activities and the antimicrobial activities of the films. In contrast, immobilized lysozyme activities and the tensile strength of the films increased. The incorporation of lysozyme did not cause significant reductions in tensile strength and elongation at break values except in films prepared with 15% CA. This study showed the good potential of asymmetric CA films to achieve controlled release in antimicrobial packaging.

a b s t r a c tIn this study, cellulose acetate (CA) films with different morphological features were prepared in order to control the release rates of low molecular weight natural antioxidants, L-ascorbic acid and L-tyrosine. Increasing CA content in the casting solution decreased the average pore size and porosity of the films, thus, reduced the diffusion rates of both antioxidants through the films. Although both antioxidants have similar molecular weights, L-tyrosine released into water much more slowly than L-ascorbic acid. The highest antioxidant activity in release test solutions was observed with highly porous L-tyrosine containing films. However, when the porosity of the films reduced, the antioxidant activity of L-ascorbic acid released into solution was found to be higher due to trapping of significant amount of L-tyrosine in dense films. The use of different antioxidants caused different changes in morphological and mechanical properties of the CA films. Varying the structural features of the films with the preparation conditions or using different surfaces of the films allowed the controlled release of each antioxidant.