No abstract

No abstract

No abstract

No abstract

No abstract

Polyethylene terephthalate (PET) nanocomposite films were prepared by cast extrusion followed by uniaxial stretching, using chill rolls. Transmission electron microscopy (TEM) and wide angle X‐ray diffraction (WAXD) showed that the clay layers were aligned in the machine direction (MD) in the PET/clay nanocomposite (PCN) films. Differential scanning calorimetry (DSC) showed that PCN films have higher crystallinity than the neat PET films, possibly due to the nucleating role of the silicate layers. The PCN films became hazier as the clay content increased, but the film transparency remained in the acceptable range. Oxygen permeability of the PCN films decreased by 23% compared to the neat PET film. This is comparable with predictions of models proposed in the literature. Silicate incorporation brought about 20% increase in the tensile modulus, while the puncture and tear propagation resistance were reduced, due to brittleness of the PCN films. The measured modulus (1.7 GPa) was somewhat smaller than the values predicted using the Pseudoinclusion model (2.1 GPa). POLYM. ENG. SCI., 2012. © 2011 Society of Plastics Engineers

In this study, rheological, crystal structure, barrier, and mechanical properties of polyamide 6 (PA6), poly(m‐xylene adipamide) (MXD6) and their in situ polymerized nanocomposites with 4 wt % clay were studied. The extent of intercalation and exfoliation as well as type of crystals, crystallinity, and thermal transitions were investigated using X‐ray diffraction (XRD) and differential scanning calorimetry (DSC), respectively. Dynamic rheological measurements revealed that incorporation of nanoclay significantly increases complex viscosity of MXD6 nanocomposites at low frequencies, which was related to the formation of a nanoclay network and exchange reaction between MXD6 chains. The comparative study of dynamic characteristics (G′ (ω) and G″ (ω)) for aliphatic and aromatic polyamide nanocomposites with their neat resins as well as the relaxation spectra for both polymer systems confirmed the possibility of the aforementioned phenomena. Although, the crystallinity of MXD6 films was lower as compared to PA6 films, the permeability to oxygen was more than 5 times better for the former. Incorporating 4 wt% clay enhanced the barrier property, tensile modulus, and yield stress of PA6 and MXD6 nanocomposite films in both machine and transverse directions without sacrificing much puncture and tear resistances. The PA6‐based films showed higher tear and puncture strength as compared to MXD6 films. POLYM. ENG. SCI., 54:2617–2631, 2014. © 2013 Society of Plastics Engineers

Blends of a long‐chain branched polypropylene (LCB‐PP) and a linear polypropylene (L‐PP) were prepared using a twin‐screw extruder. Linear viscoelastic properties such as complex viscosity, storage modulus, and weighted relaxation spectrum were determined as functions of LCB‐PP content. Shear data obtained from commercial rheometers as well as from a slit‐die rheometer were used to verify the Cox‐Merz relation for the neat components as well as for a blend. Elongational properties were obtained using a Sentmanat Extensional Rheometer (SER) unit mounted on an Advanced Rheometric Expansion System (ARES) rheometer and the converging die. A significant strain hardening was observed for the neat LCB‐PP as well as for all the blends, but the strain hardening decreased with increasing strain rate. The apparent steady elongational viscosity values evaluated using the converging die were observed to be comparable at high deformation rates to those obtained from the SER unit, but the differences increased as the strain rate decreased. POLYM. ENG. SCI., 2010. © 2009 Society of Plastics Engineers