Building‐integrated photovoltaic (BIPV), especially in a semitransparent and/or see‐through configuration, has attracted significant attention because of the extended surfaces available for the photovoltaic (PV) installation including roofs, facades, and windows. In this study, we examine the P4 scribing process for fabricating see‐through cells on a new Cu (In,Ga)Se2 (CIGS) architecture with indium tin oxide (ITO) bottom contact, using a nanosecond laser beam of 532‐nm wavelength illuminated from glass substrate side. Through parametric studies with the variations of laser beam spot size and pulse energy, we have identified that enlarged laser beam with the pulse energy near scribing threshold could suppress both damage in ITO and electrical shunt induced by molten CIGS. Scanning electron microscopy (SEM) and energy‐dispersive X‐ray spectroscopy (EDS) analyses unveil that the molten CIGS mediated shunt mechanism, wetting the scribing edge and forming Cu‐rich metallic phase. The P4 scribing process operated near threshold fluence of enlarged laser beam clearly suppressed unwanted shunt, also minimizing the fluctuation in the desired film removal trend. Thermal analysis supports that enlarged laser beam enables scribing at reduced CIGS‐ITO interface temperature assisted by buckling‐based film delamination mechanism and also suppresses CIGS melting at scribing edge and its neighborhood. See‐through cells fabricated for the areal fraction of approximately 15% using the optimal laser scribing parameters exhibited the short circuit current reduction rate of 16.8% enabled by the low shunt resistance reduction rate of approximately 8%. Further studies are underway to elucidate precise shunt‐related scribing mechanism on the basis of the cross‐sectional analyses and time‐resolved diagnostics and to fabricate the module level see‐through PV architectures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.