Dissimilar joints between STS441, a ferritic stainless steel, and SS400, a carbon steel, were welded by GMAW (Gas Metal Arc Welding) using STS430LNb as a welding wire. The fracture behavior of the dissimilar weld was analyzed by a microstructural observation and thermo-mechanical tests. Martensite was formed at the region between SS400 and the weld metal because the Cr and Nb content in this region decreased due to the dilution of SS400 carbon steel during welding. According to results from a high temperature tensile test with a specimen aged at 900°C, it was found that the tensile strength of the dissimilar weld at high temperature was equal to that of STS441 base metal and the formation of martensite had little influence on tensile strength of the dissimilar weld at high temperature. However, in the case of thermal fatigue resistance, the dissimilar weld had an inferior thermal fatigue life to STS441 because of the presence of martensite and the softened region around the interface between the dissimilar weld metal and SS400.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.