This study examined the effect of silane and phosphate functional monomer on bond strengths between a resin-based luting agent joined to a lithium disilicate ceramic (IPS e.max) and silica (quartz) materials. The e.max and quartz specimens were assigned to 6 groups with different priming/bonding agents, namely, Clearfil Porcelain Bond Activator, Clearfil Photo Bond, Clearfil Photo Bond Universal with Clearfil Porcelain Bond Activator, Clearfil Photo Bond Catalyst with Clearfil Porcelain Bond Activator, Clearfil Photo Bond with Clearfil Porcelain Bond Activator, and unprimed. The corresponding specimens were bonded by using a resin-based luting agent (Panavia V5). Shear bond strengths were determined before and after 5,000 thermocycles. For both the e.max and quartz specimens, the Clearfil Photo Bond Universal with Clearfil Porcelain Bond Activator group had the highest pre- and post-thermocycling bond strength values. Combined use of silane in the acidic environment of a phosphate functional monomer and initiators enhances bond strength of a resin-based luting agent to e.max ceramic and quartz materials.
This study evaluated the effect of zirconia framework design on fracture load of implant-supported zirconia-based prostheses after thermal cycling and mechanical loading. Three different zirconia framework designs were investigated: uniform-thickness (UNI), anatomic (ANA), and supported anatomic (SUP) designs. Each framework was layered with feldspathic porcelain (ZAC group) or indirect composite material (ZIC group). The specimens then underwent fracture load testing after thermal cycling and cyclic loading. In the ZAC group, mean fracture load was significantly lower for UNI design specimens than for the other framework designs. In the ZIC group, there was no significant difference in mean fracture load between ANA design specimens and either UNI or SUP design specimens. To improve fracture resistance of implant-supported zirconia-based prostheses after artificial aging, uniformly thick layering material and appropriate lingual support with zirconia frameworks should be provided.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.