No abstract

The highest mean shear bond strengths were observed for acid-etched PEEK surfaces, followed by laser-irradiated, airborne particle abraded, and silicoated PEEK surfaces providing similar mean shear bond strengths. Since shear bond strengths higher than 10 MPa are considered acceptable, acid etching, laser irradiation, and airborne particle abrasion of PEEK surfaces may be considered viable surface treatment modalities for the PEEK material tested.

No abstract

Imperceptible (ΔE<1.6) and clinically acceptable color changes (ΔE<3.7) were demonstrated by the alumina ceramic system tested.

No abstract

Objective:The objective of this study is the effect of different heat polymerization conditions on the strength of polymethyl methacrylate (PMMA) resin base is unknown. Distinguishing one method that provides improved mechanical properties may be beneficial to the clinical success of complete and partial dentures and overdentures. The purpose of this study was to evaluate the effect of different polymerization methods on the flexural strength of a dental PMMA resin.Materials and Methods:Forty PMMA specimens (64 mm × 10 mm × 4 mm) were prepared with 4 different polymerization methods (n = 10); heat polymerization at 74°C for 9 h, at 100°C for 40 min, and with 620 kPa pressure at 100°C for 20 min. The remaining group of specimens was microwave polymerized at 180 W for 6 min. All specimens were thermocycled at 5°C and 55°C for 5000 times. Three-point flexure test was used to measure the flexural strength of specimens. One-way ANOVA and Tukey Honestly Significant Difference were applied to analyze the differences in flexural strengths (α = 0.05).Results:The flexural strength of heat-polymerized groups was similar. The flexural strength of microwave polymerized group was significantly different and lower than the other groups (P < 0.05).Conclusion:Polymerizing conventional heat-polymerizing PMMA resin with microwave energy resulted in a significant decrease in flexural strength. The results of this study suggest that clinicians may benefit from using heat polymerization when processing PMMA denture bases instead of microvawe polymerization when tested brand is used.

As there were observable differences between the implant types, straight placed cylindrical implants showed better stress distribution characteristics, while inclined tapering implants had better stress distribution characteristics.

Background/purpose Various restoration materials have been used to restore as onlay materials to restore highly defected molar teeth. Different mechanical and physical properties of these materials may affect the success or survival of the restoration. The purpose of this study was to evaluate the restoration materials effects on stress distribution. Materials and methods Three dimensional finite element analysis (FEA) was used to evaluate the stress concentrations and distributions at the restoration and the tooth. Maxillar first molar tooth constructed to evaluate the stress distribution and concentration levels at the restorations and the tooth structure. Two kinds of restoration materials, bulkfill composite and conventional hybrid composite was evaluated for direct method, while full ceramic and indirect composite was used for indirect method. A load of 200 N was applied on the restorations and stress levels were calculated by von Mises stress values. Results Highest stress concentration was observed at the ceramic restoration (3.77 GPa). Stress levels were 2.90 GPa for bulkfill composite and 2.14 GPa for direct and indirect composite. At the tooth structure the stress levels were 3.33 GPa, 3.18 GPa and 2.48 GPa for bulkfill, direct and indirect composites respectively. The lowest stress values was observed with the porcelain restoration (1.69 GPa). Stress concentrations at the adhesive system were 2.10 MPa for bulkfill composite, 1.35 MPa for direct and indirect composites and 1.25 Mpa for porcelain restoration. Conclusion The restoration material affects the stress levels at the restoration and the tooth while the stress concentration areas remained nearly the same.