Advanced High Strength Steels (AHSS) have been widely applied in the automotive industry as an affordable solution for car lightweighting, mainly in parts subjected to crash requirements. Heavy duty vehicle (HDV) can also benefit from the expertise learned in cars, but parts must be designed considering fatigue resistance, especially on trimmed areas, and stiffness. Mechanical surface treatments, as blasting or shot peening, help increasing fatigue life of AHSS in trimmed areas and will allow weight reduction in HDV through gauge downsizing. The expected decrease in stiffness through thickness reduction can be improved by design changes. However, scarce information about the effect of mechanical surface treatments on AHSS are available. Thus, the aim of this work is to evaluate the increment in fatigue life of two different steel grades (350 MPa, and 500MPa of yield strength) in thick sheet by means of mechanical surface treatment – sandblasting. High Cycle Fatigue [HCF] tests were conducted at alternating load [R=-1]. Residual stresses were measured by an X-ray tensometry prior fatigue tests. Also the surface roughness [Rz] and form is measured using an optical non-contact 3D microscope. On the other hand, the fracture surfaces of the test specimens were observed via scanning electron microscope (SEM) in order to determine the crack initiation points. The evaluation of fatigue life in terms of SN curves is also discussed, analysing how the sandblasting process modifies the surface roughness and introduce compressive residual stresses on the external layer of the material. Both phenomena enhance the fatigue strength of the evaluated steel grades.
Driven by current safety and weight reduction policies in the automotive sector, the development of new high strength sheet metal products has experienced unprecedented growth in the last years. With the emergence of these high strength materials, new challenges related to their limited ductility and higher cracking susceptibility have also raised. Accordingly, the development of new fracture criteria accounting for the material’s cracking resistance has become unavoidable. In this work, a new cracking resistance index (CRI) based on fracture mechanics is proposed to classify the crack propagation resistance (i.e. the fracture toughness) of high strength metal sheets. The index is based on the fracture energy obtained from tensile tests with sharp-notched specimens. The procedure is very fast and simple, comparable to a conventional tensile test, and it may be used as routine testing for quality control and material selection. The CRI is investigated for several advanced high strength steel (AHSS) sheets of 0.8-1.6 mm thickness with tensile strengths between 800 and 1800 MPa. The results show that the proposed index is suitable to rank high strength steel sheets according to their crack propagation resistance and it can be correlated to the material’s crashworthiness and edge cracking resistance.
This study presents an innovative approach for selecting high-strength materials for fatigue dimensioning parts, considering both fracture toughness and fatigue performance. Warm and hot forming processes enable the construction of high-strength parts above 1000 MPa with complex geometries, making them suitable for lightweight chassis in automotive and freight applications. This research reveals that high-strength steels can experience up to a 40% reduction in fatigue performance due to manufacturing defects introduced during punching and trimming. Fracture toughness has been proposed as a good indicator of notch sensitivity, with a strong correlation of 0.83 between fracture toughness and fatigue notch sensitivity. Therefore, by combining fracture toughness measurements and fatigue resistance obtained through the rapid fatigue test, it becomes possible to quickly identify the most fatigue-resistant materials to deal with defects. Among the nine materials analysed, warm-formed steels show promising characteristics for lightweight chassis construction, with high fatigue resistance and fracture toughness exceeding the proposed fracture threshold of 250 kJ/m2.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.