To study dislocation dynamics in a model sample, an intrinsic float zone (FZ) Si wafer is chosen as seed to initiate directional solidification. During the temperature ramp, a Von Laue diffraction spot is recorded by a camera. It provides time‐resolved information on the evolution of silicon crystalline quality and on the defect nucleation locations and dynamics. With increasing temperature, dislocations are observed to propagate through the seed starting mainly from the sample edges. The effective thermomechanical local stress is estimated as low as (1.2 ± 0.4) × 105 Pa in a thermal gradient of (1.8 ± 0.2) × 102 K m−1. The latter is sufficient to allow dislocation nucleation and motion at temperatures beyond (1523 ± 9) K. Dislocation velocity increases with temperature and reaches a maximum velocity of (3.0 ± 0.5) × 10−4 m s−1 close to the silicon melting point. From the dislocation velocity measurements as a function of temperature, an activation energy of (3.1 ± 0.6) eV is estimated and this value is discussed, along with dynamical interactions between defects and dislocations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.