Low-k Si–O–C–H composite films were prepared using bis-trimethylsilylmethane as a precursor and oxygen in a rf plasma reactor. The growth rate of the Si–O–C–H composite film followed a second-order exponential decay function. This behavior could be explained by the formation of nanosized voids due to Si–CH3 and OH-related bonds included in the film. OH-related bonds were detected in films deposited at 30 °C, but could not be observed for the films deposited above 60 °C. In contrast, Si–CH3 bonds were also detected at 30 °C, but decreased monotonically up to 210 °C and were absent of higher temperatures. After postannealing the film deposited at 30 °C, the Si–CH3 bonds were unchanged, but the OH-related bonds were easily removed. This film showed a low dielectric constant of 2.44 and leakage current density of 4.4×10−7 A/cm2 at 1 MV/cm.
Articles you may be interested inImpact of I-V behavior and estimated temperature rise on surface and tip modification of the nanocontact between a highly doped silicon scanning probe microscope tip and gold surface under ambient conditions
Articles you may be interested inEffect of fluorine on the activation and diffusion behavior of boron implanted preamorphized silicon Techniques and applications of secondary ion mass spectrometry and spreading resistance profiling to measure ultrashallow junction implants down to 0.5 keV B and BF 2
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.